Films with high pore density and regularity that are easy to manufacture by conventional large-scale technology are key components aimed for fabrication of new generations of magnetic arrays for storage media, medical scaffolds, and artificial membranes. However, potential manufacture strategies like the self-assembly of block copolymers, which lead to amazing regular patterns, could be hardly reproduced up to now using commercially feasible methods. Here we report a unique production method of nanoporous films based on the self-assembly of copper(II) ion-polystyrene-b-poly(4-vinylpyridine) complexes and nonsolvent induced phase separation. Extremely high pore densities and uniformity were achieved. Water fluxes of 890 L m -2 h -1 bar -1 were obtained, which are at least 1 order of magnitude higher than those of commercially available membranes with comparable pore size. The pores are also stimuli (pH)-responsive.

A process is described to manufacture monodisperse asymmetric pH-responsive nanochannels with very high densities (pore density >2 × 10(14) pores per m(2)), reproducible in m(2) scale. Cylindric pores with diameters in the sub-10 nm range and lengths in the 400 nm range were formed by self-assembly of metal-block copolymer complexes and nonsolvent-induced phase separation. The film morphology was tailored by taking into account the stability constants for a series of metal-polymer complexes and confirmed by AFM. The distribution of metal-copolymer micelles was imaged by transmission electron microscopy tomography. The pH response of the polymer nanochannels is the strongest reported with synthetic pores in the nm range (reversible flux increase of more than 2 orders of magnitude when switching the pH from 2 to 8) and could be demonstrated by cryo-field emission scanning electron microscopy, SAXS, and ultra/nanofiltration experiments.

An integral asymmetric membrane was fabricated in a fast and one-step process by combining the self-assembly of an amphiphilic block copolymer (PS-b-P4VP) with nonsolvent-induced phase separation. The structure was found to be composed of a thin layer of densely packed highly ordered cylindrical channels with uniform pore sizes perpendicular to the surface on top of a nonordered sponge-like layer. The as-assembled membrane obtained a water flux of more than 3200 L m–2 h–1 bar–1, which was at least an order of magnitude higher than the water fluxes of commercially available membranes with comparable pore sizes, making this membrane particularly well suited to size-selective and charge-based separation of biomolecules. To test the performance of the membrane, we conducted diffusion experiments at the physiological pH of 7.4 using bovine serum albumin (BSA) and globulin-γ, two proteins with different diameters but too close in size (2-fold difference in molecular mass) to be efficiently separated via conventional dialysis membrane processes. The diffusion rate differed by a factor of 87, the highest value reported to date. We also analyzed charge-based diffusive transport and separation of two proteins of similar molecular weight (BSA and bovine hemoglobin (BHb)) through the membrane as a function of external pH. The membrane achieved a selectivity of about 10 at pH 4.7, the isoelectric point (pI) of BSA. We then positively charged the membrane to improve the separation selectivity. With the modified membrane BSA was completely blocked when the pH was 7.0, the pI of BHb, while BHb was completely blocked at pH 4.7. Our results demonstrate the potential of our asymmetric membrane to efficiently separate biological substances/pharmaceuticals in bioscience, biotechnology, and biomedicine applications.

Polymeric membranes are attractive for CO2 separation and concentration from different gas streams because of their versatility and energy efficiency; they can compete with, and they may even replace, traditional absorption processes. Here we describe a simple and powerful method for developing nanostructured and CO2-philic polymer membranes for CO2 separation. A poly(ethylene oxide)−poly(butylene terephthalate) multiblock copolymer is used as membrane material. Smart additives such as polyethylene glycol dibutyl ether are incorporated as spacers or fillers for producing nanostructured materials. The addition of these specific additives produces CO2-philic membranes and increases the CO2 permeability (750 barrer) up to five-fold without the loss of selectivity. The membranes present outstanding performance for CO2 separation, and the measured CO2 flux is extremely high (>2 m3 m−2 h−1 bar−1) with selectivity over H2 and N2 of 10 and 40, respectively, making them attractive for CO2 capture.

No abstract