The study aimed to investigate the effect of processing temperature and the content of multi-wall carbon nanotubes (MWCNTs) on the rheological, thermal, and electrical properties of polyphenylene sulfide (PPS)/MWCNT nanocomposites. It was observed that the increase in MWCNT content influenced the increase of the complex viscosity, storage modulus, and loss modulus. The microscopic observations showed that with an increase in the amount of MWCNTs, the areal ratio of their agglomerates decreases. Thermogravimetric analysis showed no effect of processing temperature and MWCNT content on thermal stability; however, an increase in stability was observed as compared to neat PPS. The differential scanning calorimetry was used to assess the influence of MWCNT addition on the crystallization phenomenon of PPS. The calorimetry showed that with increasing MWCNT content, the degree of crystallinity and crystallization temperature rises. Thermal diffusivity tests proved that with an increase in the processing temperature and the content of MWCNTs, the diffusivity also increases and declines at higher testing temperatures. The resistivity measurements showed that the conductivity of the PPS/MWCNT nanocomposite increases with the increase in MWCNT content. The processing temperature did not affect resistivity.

The aim of this research was to improve the electrical and mechanical properties of carbon-fibre-reinforced polymers (CFRP) based on thermoplastic acrylic resin ELIUM®, by introducing single-walled carbon nanotubes (SWCNTs) into their structure. The laminates were fabricated using the infusion technique of infiltrating the carbon fabric with the mixture of acrylic resin and SWCNTs. The addition of SWCNTs improved the electrical conductivity through the thickness of the laminate by several times compared to the laminate without modification. No defects or voids were observed in the structure of the fabricated nanocomposites. The introduction of SWCNTs into the CFRP structure increased the Young’s modulus, interlaminar shear strength and impact resistance. DMA analysis showed almost no change in the glass transition temperature of the fabricated SWCNT/CFRP nanocomposites compared to the reference laminate.