Chemiresistors were constructed using 3-D silica nanospring mats coated with a contiguous film of ZnO nanocrystals. Chemiresistors with an average ZnO nanocrystal radius <3 nm, or >20 nm, were found to exhibit a relative change in conductance of a factor of 50 upon exposure to a gas flow of 20% O2 and 80% N2 with ∼500 ppm of toluene and an operational temperature of 400 °C. Samples with an average ZnO nanocrystal radius of 15 nm were found to be the most responsive with a relative conductance change of a factor of 1000. The addition of metal nanoparticles (average radius equal to 2.4 nm) onto the surface of the ZnO nanocrystals (average radius equal to 15 nm) produced a relative change in conductance of a factor of 1500. For the optimum conditions (T = 400 °C, grain size ∼15 nm) well-defined spikes in conductance to explosive vapors (TNT, TATP) were obtained for 0.1 ms exposure time at ppb levels.

Crystalline Cd(OH) 2 /CdCO 3 nanowires, having lengths in the range from 0.3 up to several microns and 5-30 nm in diameter, were synthesized by a microwave-assisted wet chemical route and used as a precursor to obtain CdO nanostructures after a suitable thermal treatment in air. The morphology and microstructure of the as-synthesized and annealed materials have been investigated by scanning electron microscopy, transmission electron microscopy, x-ray diffraction and thermogravimetry-differential scanning calorimetry. The change in morphology and electrical properties with temperature has revealed a wire-to-rod transformation along with a decreases of electrical resistance.Annealed samples were printed on a ceramic substrate with interdigitated contacts to fabricate resistive solid state sensors. Gas sensing properties were explored by monitoring CO 2 in synthetic air in the concentration range 0.2-5 v/v% (2000-50 000 ppm). The effect of annealing temperature, working temperature and CO 2 concentration on sensing properties (sensitivity, response/recovery time and stability) were investigated. The results obtained demonstrate that CdO-based thick films have good potential as novel CO 2 sensors for practical applications.

Chemiresistors (conductometric sensor) were fabricated on the basis of novel nanomaterials—silica nanosprings ALD coated with ZnO. The effects of high temperature and UV illumination on the electronic and gas sensing properties of chemiresistors are reported. For the thermally activated chemiresistors, a discrimination mechanism was developed and an integrated sensor-array for simultaneous real-time resistance scans was built. The integrated sensor response was tested using linear discriminant analysis (LDA). The distinguished electronic signatures of various chemical vapors were obtained at ppm level. It was found that the recovery rate at high temperature drastically increases upon UV illumination. The feasibility study of the activation method by UV illumination at room temperature was conducted.

No abstract