A conducting polymer, polyaniline, was synthesized by chemical polymerization using different inorganic acids, such as HCl, H2SO4, HClO4, HNO3, and H3PO4, as protonic acid media. The synthesized polymers were characterized using UV‐visible and FT‐IR spectroscopy. A granular type of morphology was observed under SEM for HCl, HNO3, and H3PO4 doped polyanilines. However, HClO4 doped polyaniline shows the folded lamellar structure derived from the fibers. The thermal stability of these polymers was investigated with the help of thermogravimetric (TG/SDTA) analysis. The formation of a greater fraction of the conducting emeraldine salt phase is observed in HClO4 as a protonic acid media. The thermal stability of H3PO4 doped material is found to be better as compared with other acids. An increase in conductivity with an increase in temperature was observed in all the samples except for HClO4 doped polyaniline. Polym. Eng. Sci. 44:1676–1681, 2004. © 2004 Society of Plastics Engineers.

Spectroscopic [UV–visible and Fourier transform IR (FTIR)] and thermal properties of chemically synthesized polyanilines are found to be affected by varying the protonation media (acetic, citric, oxalic, and tartaric acid). The optical spectra show the presence of a greater fraction of fully oxidized insulating pernigraniline phase in polyaniline doped with acetic acid. In contrast, the selectivity in the formation of the conducting phase is higher in oxalic acid as a protonic acid media. The FTIR spectra of these polymers reveal a higher ratio of the relative intensities of the quinoid to benzenoid ring modes in acetic acid doped polyaniline. Scanning electron micrographs revealed a sponge‐like structure derived from the aggregation of the small granules in acetic acid and oxalic acid doped polyaniline. A three‐step decomposition pattern is observed in all the polymers, regardless of the protonic acid used for the doping. The second step loss related to the loss of dopant is found to be higher in the oxalic acid doped polymer. In accordance with these results the conductivity is also found to be higher in oxalic acid doped material. The temperature dependent conductivity measurements show the thermal activated behavior in all the polymers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2043–2049, 2004

No abstract