Purpose Fluorine and silicon materials have received the keen attention of many researchers because of their water repellency and low surface free energy. The purpose this study was to prepare vinyl acetate (VAc)-vinyl ester of neodecanoic acid (VeoVa 10) copolymer latex modified with fluorine and silicone monomer, which is emulsified with the novel surfactants of disodium laureth sulfosuccinate (MES) and octylphenol polyoxyethylene ether (OP-10). Design/methodology/approach A series of modified latices containing fluorine-silicon have been prepared by semi-continuous seeded emulsion polymerisation of mixed monomers of VAc, VeoVa10, hexafluorobutylmethacrylate (HFMA) and vinyltriethoxysilane (VTES) and emulsified by novel surfactants of MES and OP-10. Findings The optimum conditions for preparing the modified latex is as follows: the amount of the surfactant was 4.0 Wt.% and the mass ratio of the anionic and nonionic surfactant was 3:1; the dosage of initiator was 0.4 Wt.% and the mass ratio of the main monomer was 3:1; and the amounts of VTES and HFMA were 2.0 and 6.0 Wt.%, respectively. In comparison with the conventional latex, the hydrophobicity of latex film was improved further. Originality/value The modified p (VAC-VeoVa) latex is prepared via semi-continuous seeded emulsion polymerisation, which is emulsified with the novel mixed surfactants of MES and OP-10. There are two main innovations. One is that the novel p (VAC-VeoVa) latex containing fluorine-silicon is prepared successfully. The other is that the emulsifier is composed of the novel mixed surfactants of MES and OP-10.
The polyacrylate latex has been successfully prepared by semicontinuous seeded emulsion polymerization with methyl methacrylate (MMA), butyl acrylate (BA), and acrylic acid (AA), which were initiated with potassium persulfate and emulsified with the novel green mixed surfactants of alkyl polyglycoside (APG1214) and disodium laureth sulfosuccinate (MES). The particle size of the latex was measured by Zetatrac dynamic light scattering detector. The structure of the latex was tested by Fourier-transform infrared spectroscopy. The film of latex was tested by differential scanning calorimetry and thermogravimetric analysis. Factors, which had an influence on the properties of the latex, were studied in detail. The optimum conditions for preparing the polyacrylate latex were as follows: the amount of emulsifiers was 7.0%, the mass ratio of APG1214 to MES was 3:1, the amount of the initiator was 0.7%, the mass ratio of MMA to BA was 1:1, and the amount of AA was 2.0%. In this case, the conversion of the mixed monomers was high and the mechanical and ionic stability of the latex was good.
Purpose Silane cross-linkers have been used to strengthen the mechanical stabilities and friction resistance of plastic products. Therefore, the effect of silane cross-linkers on latex has been studied through preparing modified self-cross-linking long fluorocarbon polyacrylate latex. In this paper, nonionic surfactant alcohol ether glycoside (AEG1000) and anionic polymerizable surfactant 1-allyloxy-3-(4-nonylphenol)-2-propanol polyoxyethylene (10) ether ammonium sulfate (DNS-86) acted as mixed emulsifier and 3-(methacryloyloxy) propyltrimethoxysilane (KH-570) and bis (2-ethylhexyl) maleate (DOM) were used as functional monomers. Design/methodology/approach The modified acrylate polymer latex was synthesized through the semi-continuous seeded emulsion polymerization with methyl methacrylate (MMA), butyl acrylate (BA), dodecafluoroheptyl methacrylate (DFMA) and hydroxypropyl methacrylate (HPMA) as main monomers. Potassium persulfate (KPS) was applied to initiate polymerization reaction, nonionic surfactant AEG1000 and DNS-86 acted as emulsifier, KH-570 and DOM were used as functional monomers, respectively. Findings The optimum conditions of synthesizing the modified latex were the following. The mass ratio of monomers containing MMA, BA, DFMA, HPMA, KH-570 and DOM was 13.58:13.58:0.90:1.20:0.15:0.60, the usage of initiator KPS was 0.5% of the total weight of monomers and the amount of emulsifier was 7% of all monomers with AEG1000:DNS-86 = 1:1. The results indicated that the conversion of monomer was 99% and the coagulation was about 2.0%. Originality/value The resultant latex was modified silane cross-linker KH-570 and DOM, which positively affected the comprehensive properties of latex and its film. Apart from this, the novel mixed emulsifier was used to improve the size and distribution of latex particles and reduce environmental problems caused by the use of emulsifiers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.