A new series of metal chalcogenides with the formula Ba6Ag2.67+4δSn4.33−δS16–x Se x (x = 0 for 1, x = 6.47 for 2, and x = 16 for 3) were synthesized. Compounds 1–3 are isotypic with a three-dimensional structure and crystallize in the noncentrosymmetric space group I4̅3d. The framework in 1 is constructed by alternative corner-sharing of AgS4 and SnS4 tetrahedra with Ba2+ cations distributed within the channels. The Ag+ atoms are disordered with two neighboring silver sites trapped in various coordination environments. Selected area electron diffraction (SAED) patterns from samples of 1 indicate that the structural lattice is ordered without evidence of long-range ordering. High resolution electron microscopy (HREM) images of 1 along the [001] direction display the body-centered arrangement of barium atoms and the periodic appearance of lines between barium atoms that correspond to part of the array of disordered silver atoms. Within the sulfide composition range, the solid solutions are Ba6Ag2.67+4δSn4.33−δS16 with δ = 0.13 for 1, 0.31 for 1a, and 0.33 for 1b; the crystal colors range from dark-red to orange and yellow, respectively. All compounds are transparent in the mid-infrared region and have absorption edges ranging from 1.27 to 2.37 eV. The significant second harmonic generation (SHG) intensities of the five materials are optimized at wavelengths ranging from 600 to 800 nm. The outstanding ones are 1a and 2 which display strong intensities 4.4–11.6 times and 2.2–10.4 times that of AgGaSe2 in the ranges 600–700 nm and 675–800 nm, respectively. Raman spectroscopic characterization is reported.
We synthesized the barium/strontium solid solution sequence Ba 6−x Sr x [Ag (4−y) Sn (y/4) ](SnS 4) 4 for nonlinear optical (NLO) applications in the infrared (IR) via a flux synthesis route. All title compounds are isotypic, crystallizing in the cubic space group I 3d and are composed of a three-dimensional (3D) anionic framework of alternating corner-sharing SnS 4 and AgS 4 tetrahedra charge balanced by Ba and Sr. The shrinkage of Ba/Sr-S bond lengths causes the tetrahedra in the anionic framework to become more distorted, which results in a tunable band gap from 1.58 to 1.38 eV with increasing x values. The performance of the barium limit (x = 0) is also superior to that of Sr (x = 6), but surprisingly second harmonic generation (SHG) of the solid solution remains strong and is insensitive to the value of x over the range 0 to 3.8. Results show that the non-type-I phase-matched SHG produced by these cubic chalcogenides display intensities higher than the benchmark AgGaSe 2 from 600-1000 nm.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.