Aluminum 1,4-benzenedicarboxylate Al(OH)[O(2)C-C(6)H(4)-CO(2)]. [HO(2)C-C(6)H(4)-CO(2)H](0.70) or MIL-53 as (Al) has been hydrothermally synthesized by heating a mixture of aluminum nitrate, 1,4-benzenedicarboxylic acid, and water, for three days at 220 degrees C. Its 3 D framework is built up of infinite trans chains of corner-sharing AlO(4)(OH)(2) octahedra. The chains are interconnected by the 1,4-benzenedicarboxylate groups, creating 1 D rhombic-shaped tunnels. Disordered 1,4-benzenedicarboxylic acid molecules are trapped inside these tunnels. Their evacuation upon heating, between 275 and 420 degrees C, leads to a nanoporous open-framework (MIL-53 ht (Al) or Al(OH)[O(2)C-C(6)H(4)-CO(2)]) with empty pores of diameter 8.5 A. This solid exhibits a Langmuir surface area of 1590(1) m(2)g(-1) together with a remarkable thermal stability, since it starts to decompose only at 500 degrees C. At room temperature, the solid reversibly absorbs water in its tunnels, causing a very large breathing effect and shrinkage of the pores. Analysis of the hydration process by solid-state NMR ((1)H, (13)C, (27)Al) has clearly indicated that the trapped water molecules interact with the carboxylate groups through hydrogen bonds, but do not affect the hydroxyl species bridging the aluminum atoms. The hydrogen bonds between water and the oxygen atoms of the framework are responsible for the contraction of the rhombic channels. The structures of the three forms have been determined by means of powder X-ray diffraction analysis. Crystal data for MIL-53 as (Al) are as follows: orthorhombic system, Pnma (no. 62), a = 17.129(2), b = 6.628(1), c = 12.182(1) A; for MIL-53 ht (Al), orthorhombic system, Imma (no. 74), a = 6.608(1), b = 16.675(3), c = 12.813(2) A; for MIL-53 lt (Al), monoclinic system, Cc (no. 9), a = 19.513(2), b = 7.612(1), c = 6.576(1) A, beta = 104.24(1) degrees.

We report on Pb,Br, N,H, C andH NMR experiments for studying the local order and dynamics in hybrid perovskite lattices. Pb NMR experiments conducted at room temperature on a series of MAPbX compounds (MA = CHNH; X = Cl, Br and I) showed that the isotropic Pb NMR shift is strongly dependent on the nature of the halogen ions. ThereforePb NMR appears to be a very promising tool for the characterisation of local order in mixed halogen hybrid perovskites. Pb NMR on MAPbBrI served as a proof of concept. Proton, C andN NMR experiments confirmed the results previously reported in the literature. Low temperature deuterium NMR measurements, down to 25 K, were carried out to investigate the structural phase transitions of MAPbBr. Spectral lineshapes allow following the successive phase transitions of MAPbBr. Finally, quadrupolar NMR lineshapes recorded in the orthorhombic phase were compared with simulated spectra, using DFT calculated electric field gradients (EFG). Computed data do not take into account any temperature effect. Thus, the discrepancy between the calculated and experimental EFG evidences the fact that MA cations are still subject to significant dynamics, even at 25 K.