The study is carried out to understand the new corrosion protection technique, non-polarization concept, using current/voltage pulses to achieve a potential of zero charges (Epzc) of the metal-solution interface. As a result, a cost-saving and ecological method has been proposed as a new anti-corrosion method. In the methodology, U-bend samples are immersed in a 3.5% NaCl solution with different pH values. The readings prove the occurrence of electrochemical reaction, absence of charges, and the effect of Epzc. An examination on the ZCCP on low-carbon steel in 3.5% NaCl solution was analyze for 120 hours days. This study is carried out to understand the concept of corrosion behaviour and a new corrosion protection technique which applies non-polarization concept. A U-bend mild steel is used to corrosion effect in various pH values under zero charge protection. Samples were then immersed in 3.5% NaCl solution with different pH values. Electrochemical behaviour of steel sample in 3.5% NaCl solution was analysed by means of Tafel extrapolation. It was found that Ecorr and icorr recorded dissimilar readings at different pH values. As Ecorr rises, icorr drops from pH 6 to pH 9, hence corrosion rate also decreases from pH 6 to pH 9. Zero charge corrosion protection (ZCCP) technique is used to study the efficiency of corrosion protection method in different pH values. Readings of alternating current (IAC) and direct voltage (VDC) are recorded throughout the ZCCP experiment. These readings prove the occurrence of electrochemical reaction, absence of charges and the effect of Epzc.