This research investigated the influence of stearic acid on the injection molding of alumina, by varying the concentration of stearic acid. The interaction between stearic acid and alumina was identified using transmission infrared spectroscopy, indicating stearic acid preferentially adsorbed onto the alumina powder surface. In addition to slightly modifying the intrinsic binder viscosity, stearic acid adsorbed onto the powder surface changed the flow behavior of the mixtures from dilatant flow to pseudoplastic flow at low temperatures. As a result, inhomogeneous distribution of binder in the injection‐molded parts was minimized with increased stearic acid concentration. However, the possibility of forming bubbles in the mixtures arising from vaporization of stearic acid was enhanced. Additionally, the binder burnout temperature range was broadened with the increase of stearic acid concentration.