HiPco single-wall carbon nanotubes (SWNTs) have been noncovalently modified with ionic pyrene and naphthalene derivatives to prepare water-soluble SWNT polyelectrolytes (SWNT-PEs), which are analogous to polyanions and polycations. The modified nanotubes have been characterized with UV-vis-NIR, fluorescence, Raman and X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). The nanotube-adsorbate interactions consist of pi-pi stacking interactions between the aromatic core of the adsorbate and the nanotube surface and specific contributions because of the substituents. The interaction between nanotubes and adsorbates also involves charge transfer from adsorbates to SWNTs, and with naphthalene sulfonates the role of a free amino group was important. The ionic surface charge density of the modified SWNTs is constant and probably controlled by electrostatic repulsion between like charges. The linear ionic charge density of the modified SWNTs is similar to that of common highly charged polyelectrolytes.

Electronically conducting polyanion and polycation based on poly(alkoxythiophene) derivatives, poly-3-(3'-thienyloxy)propanesulfonate (P3TOPS) and poly-3-(3'-thienyloxy)propyltriethylammonium (P3TOPA) have been synthesized. Both polymers are water-soluble and exhibit high conjugation length in solution and in the solid state. These polyelectrolytes were used to prepare conducting and electroactive polyelectrolyte multilayers by the sequential layer-by-layer adsorption technique. In aqueous solutions multilayers of P3TOPS with inactive polyelectrolytes (e.g., poly(diallyldimethylammonium chloride), PDADMA) displayed electrochemical and optical behavior similar to polythiophene films prepared in organic media. Their in-plane conductivity was low (ca. 1.6 x 10(-)(5) S cm(-)(1)). The conductivity could, however, be increased by a factor of ca. 40 in "all-thiophene" films, in which P3TOPA was substituted for the inactive polycation (PDADMA). The interpenetration of layers is of prime importance in films containing conducting components. The interpenetration of P3TOPS was studied by measuring the charge-transfer rate across an insulating polyelectrolyte multilayer between the substrate and the P3TOPS layer with modulated electroreflectance. The extent of interpenetration was 8-9 polyelectrolyte layers, the length scale (7-15 nm) depending on the nature of the insulating layer and, especially, on the ionic strength of the solution used for the adsorption of P3TOPS.

We have used anionic and cationic single-wall carbon nanotube polyelectrolytes (SWNT-PEs), prepared by the noncovalent adsorption of ionic naphthalene or pyrene derivatives on nanotube sidewalls, for the layer-by-layer self-assembly to prepare multilayers from carbon nanotubes with polycations, such as poly(diallyldimethylammonium) or poly(allylamine hydrochloride) (PDADMA or PAH, respectively), and polyanions (poly(styrenesulfonate), PSS). This is a general and powerful technique for the fabrication of thin carbon nanotube films of arbitrary composition and architecture and allows also an easy preparation of all-SWNT (SWNT/SWNT) multilayers. The multilayers were characterized with vis-near-IR spectroscopy, X-ray photoelectron spectroscopy (XPS), surface plasmon resonance (SPR) measurements, atomic force microscopy (AFM), and imaging ellipsometry. The charge compensation in multilayers is mainly intrinsic, which shows the electrostatic nature of the self-assembly process. The multilayer growth is linear after the initial layers, and in SWNT/polyelectrolyte films it can be greatly accelerated by increasing the ionic strength in the SWNT solution. However, SWNT/SWNT multilayers are much more inert to the effect of added electrolyte. In SWNT/SWNT multilayers, the adsorption results in the deposition of 1-3 theoretical nanotube monolayers per adsorbed layer, whereas the nominal SWNT layer thickness is 2-3 times higher in SWNT/polyelectrolyte films prepared with added electrolyte. AFM images show that the multilayers contain a random network of nanotube bundles lying on the surface. Flexible polyelectrolytes (e.g., PDADMA, PSS) probably surround the nanotubes and bind them together. On macroscopic scale, the surface roughness of the multilayers depends on the components and increases with the film thickness.

Molecular photon upconversion luminescence was observed from an ion-associated complex of an erbium chelate of 2-thenoyltrifluoroacetone and a near-infrared-emitting cyanine dye in anhydrous solution at room temperature. In the complex erbium was sensitized by the organic antenna dye excited at 808 nm. The result was characteristic erbium emission at 510−565 nm with second-order dependence on the excitation power, suggesting a dye-sensitized energy transfer upconversion mechanism. Compared to inorganic upconverting nanoparticles, the organic molecular dye-sensitized complexes are expected to offer higher molar absorptivity, smaller well-defined size, and simpler addition of functional groups.