Self-assembling building blocks that are readily functionalizable and capable of achieving programmed hierarchical organization have enabled us to create various functional nanomaterials. We have previously demonstrated that N,N'-disubstituted 4,6-diaminopyrimidin-2(1 H)-one (DAP), a guanine-cytosine hybridized molecule, is a versatile building block for the creation of tapelike supramolecular polymer species in solution. In the current study, DAP was functionalized with azobenzene side chains. 1H NMR, UV/Vis, and dynamic light scattering studies confirmed the presence of nanometer-scale tapelike supramolecular polymers in alkane solvents at micromolar regimes. At higher concentrations (millimolar regimes), the supramolecular polymers hierarchically organized into lamellar superstructures to form organogels, as shown by X-ray diffraction and polarized optical microscopy. Remarkably, the azobenzene side chains are photoisomerizable even in the supramolecular polymers, owing to their loosely packed state supported by the rigid hydrogen-bonded scaffold, enabling us to establish photocontrollable supramolecular polymerization and higher order organization of the tapelike supramolecular polymers into lamellar superstructures.

Bis- and monoureas hybridized with the oligo(p-phenylene vinylene) (OPV) pi-electronic segment and 3,4,5-tridodecyloxyphenyl wedge were synthesized and their supramolecular polymerization in diluted solution, gel formation in concentrated solution, and liquid crystallinity in bulk state were investigated. Bisurea 1a featuring a hexamethylene linker showed the highest supramolecular polymerization ability and formed tapelike nanofibers that can gelate various organic solvents. On the other hand, bisurea 1b featuring a dodecamethylene linker and monourea 2 showed a lower degree of supramolecular polymerization, resulting in gel formations in a smaller variety of solvents. These results clearly reflect a high level of cooperativity between the two urea sites and the two OPV segments of 1a upon hydrogen-bonding and pi-pi stacking interactions, respectively. When the gels of 1a, 1b, and 2 were dried, all the compounds self-organized into multilamellar superstructures. Thermal treatment of these lamellae at high temperatures induces columnar liquid-crystalline mesophases as a result of microsegregation between the rigid OPV parts and the molten aliphatic wedges. These results demonstrate that the present molecular constituent is very useful for fabricating dye-based functional assemblies providing nanoscale pi-electronic fibers, and solvent-incorporated and bulk soft materials.

No abstract