The purpose of this study was to investigate the effect of phase compositions of porous calcium phosphate (CaP) ceramics on their protein adsorption behaviors in vitro and osteoinductive potentials in vivo in mice. Under competitive conditions, a high adsorption of bone morphogenetic protein 2 (BMP-2) was observed at a high initial concentration of BMP-2 in the multi-protein solution on all the four types of ceramics, indicating their strong affinity for BMP-2. No significant difference in BMP-2 adsorption between the ceramics was noted, indicating that phase composition could have little influence on BMP-2 adsorption. After implantation into the thigh muscles of mice for 45 and 90 days, the histological and histomorphometric analyses showed that porous biphasic calcium phosphate (BCP) ceramic consisting of 30% hydroxyapatite HA and 70% tricalcium phosphate (β-TCP), i.e. BCP-2 had stronger osteoinductive ability than the other three groups of ceramics. The immunohistochemical staining showed the highest expression of BMP-2 and osteocalcin (OCN) in BCP-2 group. Osteoinduction of porous CaP ceramics might be influenced by the amount of BMP-2 present in the local microenvironment in the implant, which was regulated by the phase composition of the ceramics. BCP-2 promoted the highest expression of BMP-2 and then showed the strongest osteoinduction in mice.

Icariin can be a potential promoting compound for cartilage tissue engineering, and it can be a substitute for the use of some growth factors. The long history and extensive cases of safe use in China, Japan and Korea make it more attractive.

The network structure of a three-dimensional hydrogel scaffold dominates its performance such as mechanical strength, mass transport capacity, degradation rate and subsequent cellular behavior. The hydrogels scaffolds with interpenetrating polymeric network (IPN) structure have an advantage over the individual component gels and could simulate partly the structure of native extracellular matrix of cartilage tissue. In this study, to develop perfect cartilage tissue engineering scaffolds, IPN hydrogels of collagen/chondroitin sulfate/hyaluronan were prepared via two simultaneous processes of collagen self-assembly and cross linking polymerization of chondroitin sulfate-methacrylate (CSMA) and hyaluronic acid-methacrylate. The degradation rate, swelling performance and compressive modulus of IPN hydrogels could be adjusted by varying the degree of methacrylation of CSMA. The results of proliferation and fluorescence staining of rabbit articular chondrocytes in vitro culture demonstrated that the IPN hydrogels possessed good cytocompatibility. Furthermore, the IPN hydrogels could upregulate cartilage-specific gene expression and promote the chondrocytes secreting glycosaminoglycan and collagen II. These results suggested that IPN hydrogels might serve as promising hydrogel scaffolds for cartilage tissue engineering.

A collagen type I hydrogel was constructed and used as the scaffold for cartilage tissue engineering. Neonatal rabbit chondrocytes were seeded into the hydrogel, and the constructs were cultured in vitro for 7, 14, and 28 days. The immunomodulatory effect of the hydrogel on seeded chondrocytes was carefully investigated. The expressions of major histocompatibility complex classes I and II of seeded chondrocytes increased with the time, which indicated that the immunogenicity also increased with the time. Meanwhile, the properly designed collagen type I hydrogel could prompt the chondrogenesis of engineered cartilage. The extracellular matrix (ECM) synthesis ability of seeded chondrocytes and the accumulated ECM in the constructs continuously increased with the culture time. Both the isolation and protection, which come from formed ECM and hydrogel scaffold, can effectively control the adverse immunogenicity of seeded chondrocytes and even help to lessen the immunogenicity of the whole engineered cartilage. As the result, the levels of mixed lymphocyte chondrocyte reactions of seed cells and the constructs decreased gradually. The stimulation on allogeneic lymphocytes of the whole constructs was obviously lower than that of the retrieved cells from the constructs. Therefore, properly designed collagen type I hydrogel can give certain immunogenicity-reducing effects on engineered cartilage based on chondrocytes, and it may be a potential immunomodulatory biomaterial in tissue engineering.

No abstract