The microstructure and phase composition of a cast Ti 15.4 Zr 30.2 Mn 44 V 5.4 Сr 5 alloy obtained using titanium sponge, as well as the phase composition of hydrogenation product, are investigated by scanning electron microscopy and X-ray phase analysis. As found, the complete replacement of expensive iodide titanium with a relatively cheap titanium sponge does not affect the structure and phase composition of the alloy. As shown, the saturation of the alloy with hydrogen occurs at room temperature and pressure of hydrogen of 0.21 MPa in a short time up to a capacity of 2.12% mass.

No abstract

Îòòèñêè äîñòóïíû íåïîñðåäñòâåííî îò èçäàòåëÿ Ôîòîêîïèðîâàíèå ðàçðåøåíî òîëüêî â ñîîòâåòñòâèè ñ ëèöåíçèåé 2018 ÈÌÔ (Èíñòèòóò ìåòàëëîôèçèêè èì. Ã. Â. Êóðäþìîâà ÍÀÍ Óêðàèíû) Íàïå÷àòàíî â Óêðàèíå. 650 Т. В. ПРЯДКО, В. А. ДЕХТЯРЕНКО МПа. Також встановлено, що хром зменшує термічну стабільність одержаного гідриду, розпад якого розпочинається за кімнатної температури, а максимальна реверсна місткість досягається при 300 C.

Методами оптической и сканирующей электронной микроскопии с ис-пользованием энергодисперсионного анализа EDAX, рентгеновского фа-зового и дифференциального термического анализов изучено влияние ча-стичной замены ванадием компонентов эвтектического сплава 47,5 Ti-30 Zr-22,5 Mn на его структуру, фазовый и химический состав. Установ-лено, что легирование приводит к повышению температуры плавления эвтектической составляющей, к увеличению объёмной доли -фазы, к снижению содержания Mn в -фазе, а также сдвигает границу области гомогенности интерметаллида (Ti,Zr)(Mn,V) 2 в сторону титана.Методами оптичної та сканівної електронної мікроскопії з використан-ням енергодисперсійного аналізу EDAX, Рентґенового фазового та дифе-ренційного термічного аналізів вивчено вплив часткової заміни ванадієм компонентів евтектичного стопу 47,5 Ti-30 Zr-22,5 Mn на його структу-ру, фазовий і хімічний склад. Встановлено, що леґування призводить до підвищення температури топлення евтектичної складової, до збільшення об'ємної частки -фази, до пониження вмісту Mn у -фазі, а також зсуває межу області гомогенності інтерметаліду (Ti,Zr)(Mn,V) 2 у бік титану.The influence of partial substitution of components of the 47.5 Ti-30 Zr-22.5 Mn eutectic alloy with vanadium on the alloy structure, phase and chemical composition is studied by means of the optical and scanning electron microscopy with using energy-dispersive EDAX analysis, X-ray phase and differential thermal analyses. As revealed, the alloying with vanadium leads to increase of the temperature of the eutectic melting, increase of the -phase volume fraction, and decrease of the Mn content in -phase, and also shifts the boundary of a homogeneity region of the intermetallic (Ti,Zr)(Mn,V) 2 compound towards titanium.Ключевые слова: эвтектические сплавы, интерметаллид, твёрдый рас-твор, термическая обработка. Металлофиз. новейшие технол. / Metallofiz. Noveishie Tekhnol. 2014, т. 36, № 6, сс. 803-813 Оттиски доступны непосредственно от издателя Фотокопирование разрешено только в соответствии с лицензией 2014 ИМФ (Институт металлофизики им. Г. В. Курдюмова НАН Украины) Напечатано в Украине.

Sorption properties and kinetic parameters of hydrogenating and dehydrogenating processes of Ti 0.475 Zr 0.3 Mn 0.225 eutectic alloy, in which partial substitution of each of its component with 2% and 5% of vanadium is performed, are investigated by Sieverts' method. As determined, the introduction of vanadium within the specified limits results in decrease of the temperature of the start of intensive hydrogen absorption, decrease of the duration of hydrogenating process, and also in substantial increase of sorption capacity (up to 2.85% wt.). As shown, the alloys, which are subjected to the sorptiondesorption cycling, possess as much activated surface that behave themselves with regard to hydrogen similar to intermetallic compounds and can absorb hydrogen at the room temperature and the pressure of 0.23 MPa from the first seconds of the contact of the specimen with the hydrogen-containing medium with the average rate of (2-4)10 3 wt.%/s. Сівертсовою методою досліджено сорбційні властивості і кінетичні параметри процесів гідрування і дегідрування виливаного евтектичного стопу Ti 0,475 Zr 0,3 Mn 0,225 , в якому було виконано часткову заміну кожного з його компонентів на 2% і 5% Ванадію. Встановлено, що введення Ванадію в зазначених межах приводить до зниження температури початку інтенсивного вбирання Гідроґену, зменшення тривалости процесу гідрування, а також до істотного збільшення сорбційної місткости (до 2,85% мас.). Показано, що стопи, які пройшли циклування сорбція-десорбція, мають настільки активовану поверхню, що ведуть себе щодо водню неначе інтерметаліди і здатні вбирати Гідроґен за кімнатної температури і тиску у 0,23 МПа з перших секунд контакту зразка з водневим середовищем із середньою швидкістю у (2-4)10 3 мас.%/с. Методом Сивертса исследованы сорбционные свойства и кинетические параметры процессов гидрирования и дегидрирования литого эвтектического сплава Ti 45,5 Zr 30 Mn 22,5 , в котором была произведена частичная замена каждого из его компонентов на 2% и 5% ванадия. Установлено, что