UiO-66 is a highly important prototypical zirconium metal−organic framework (MOF) compound because of its excellent stabilities not typically found in common porous MOFs. In its perfect crystal structure, each Zr metal center is fully coordinated by 12 organic linkers to form a highly connected framework. Using high-resolution neutron power diffraction technique, we found the first direct structural evidence showing that real UiO-66 material contains significant amount of missing-linker defects, an unusual phenomenon for MOFs. The concentration of the missinglinker defects is surprisingly high, ∼10% in our sample, effectively reducing the framework connection from 12 to ∼11. We show that by varying the concentration of the acetic acid modulator and the synthesis time, the linker vacancies can be tuned systematically, leading to dramatically enhanced porosity. We obtained samples with pore volumes ranging from 0.44 to 1.0 cm 3 / g and Brunauer−Emmett−Teller surface areas ranging from 1000 to 1600 m 2 /g, the largest values of which are ∼150% and ∼60% higher than the theoretical values of defect-free UiO-66 crystal, respectively. The linker vacancies also have profound effects on the gas adsorption behaviors of UiO-66, in particular CO 2 . Finally, comparing the gas adsorption of hydroxylated and dehydroxylated UiO-66, we found that the former performs systematically better than the latter (particularly for CO 2 ) suggesting the beneficial effect of the −OH groups. This finding is of great importance because hydroxylated UiO-66 is the practically more relevant, non-air-sensitive form of this MOF. The preferred gas adsorption on the metal center was confirmed by neutron diffraction measurements, and the gas binding strength enhancement by the −OH group was further supported by our firstprinciples calculations. ■ INTRODUCTIONMetal−organic frameworks (MOFs), consisting of inorganic metal centers connected by organic linkers, are a relatively new family of porous materials that possess rich chemistry and offer great promise for gas adsorption related applications.

We have examined the methane uptake properties of six of the most promising metal organic framework (MOF) materials: PCN-14, UTSA-20, HKUST-1, Ni-MOF-74 (Ni-CPO-27), NU-111, and NU-125. We discovered that HKUST-1, a material that is commercially available in gram scale, exhibits a room-temperature volumetric methane uptake that exceeds any value reported to date. The total uptake is about 230 cc(STP)/cc at 35 bar and 270 cc(STP)/cc at 65 bar, which meets the new volumetric target recently set by the Department of Energy (DOE) if the packing efficiency loss is ignored. We emphasize that MOFs with high surface areas and pore volumes perform better overall. NU-111, for example, reaches ~75% of both the gravimetric and the volumetric targets. We find that values for gravimetric uptake, pore volume, and inverse density of the MOFs we studied scale essentially linearly with surface area. From this linear dependence, we estimate that a MOF with surface area 7500 m(2)/g and pore volume 3.2 cc/g could reach the current DOE gravimetric target of 0.5 g/g while simultaneously exhibiting around ~200 cc/cc volumetric uptake. We note that while values for volumetric uptake are based on ideal single crystal densities, in reality the packing densities of MOFs are much lower. Finally, we show that compacting HKUST-1 into wafer shapes partially collapses the framework, decreasing both volumetric and gravimetric uptake significantly. Hence, one of the important challenges going forward is to find ways to pack MOFs efficiently without serious damage or to synthesize MOFs that can withstand substantial mechanical pressure.