F-La/TiO2 photocatalysts were studied in photocatalytic decomposition water-methanol solution. The structural, textural, optical, and electronic properties of F-La/TiO2 photocatalysts were studied by combination of X-ray powder diffraction (XRD), nitrogen physisorption, Ultraviolet–visible diffuse reflectance spectroscopy (UV-Vis DRS), Electrochemical impedance spectroscopy (EIS), and X-ray fluorescence (XPS). The production of hydrogen in the presence of 2.8F-La/TiO2 was nearly up to 3 times higher than in the presence of pure TiO2. The photocatalytic performance of F-La/TiO2 increased with increasing photocurrent response and conductivity originating from the higher amount of fluorine presented in the lattice of TiO2.

The study compares the photocatalytic behavior of TiO2, NiO-TiO2, and Ni-NiO-TiO2 photocatalysts in photocatalytic hydrogen production from methanol–water solution. TiO2 and NiO-TiO2 photocatalysts with theoretical NiO loading of 0.5, 1.0, and 3.0 wt. % of NiO were prepared by the sol–gel method. The Ni-NiO-TiO2 photocatalysts were prepared by partial reduction of NiO-TiO2 in hydrogen at 450 °C. The Ni-NiO-TiO2 photocatalysts showed significantly higher hydrogen production than the NiO-TiO2 photocatalysts. The structural, textural, redox, and optical properties of all of the prepared photocatalysts were studied by using XRD, SEM, N2- adsorption, XPS, H2-TPR, and DRS. Attention is focused on the contribution of Ni loading, the surface composition (Ni2+, the lattice O2− species, and OH groups), the distribution of Ni species (dispersed NiO species, crystalline NiO phase, and the metallic Ni0 species), oxygen vacancies, TiO2 modification, the TiO2 crystallite size, and the specific surface area.

A memory effect is the ability to restore the original, lamellar layered double hydroxide structure. Herein, we have described 1) the changes in the structural and basic properties of ZnAl mixed oxides during their transformation into ZnAl-reconstructed LDHs (RE-LDHs); 2) the extraordinary properties of ZnAl RE-LDHs compared to the original ZnAl LDHs; and 3) the changes of basic properties during the interaction of ZnAl RE-LDHs with atmospheric CO2. Aldol condensation was selected as probe reaction to prove the catalytic potential of ZnAl RE-LDHs. We have described a target method for preparing ZnAl RE-LDHs with a large number of basic sites. ZnAl RE-LDHs possess significantly higher furfural conversion in the aldol condensation of furfural than MOs. The structural, textural, and basic properties of the studied materials were described by temperature-programmed analysis, X-ray diffraction, N2 adsorption, temperature-programmed desorption of CO2, and in-situ diffuse reflectance spectroscopy.