Gadolinium oxide host and europium/dysprosium/terbium doped gadolinium oxide nanoparticles were synthesized using the sonochemical technique. Gadolinium oxide nanocrystals were also co-doped with total 2 mol% of Eu(3+)/Dy(3+),Eu(3+)/Tb(3+),Dy(3+)/Tb(3+), and also Eu(3+)/Dy(3+)/Tb(3+) ions, by the same method. The nanoparticles obtained were characterized using powder x-ray diffraction (XRD), transmission electron microscopy (TEM), and selected area electron diffraction (SAED) techniques. The size of the particles ranged from 15 to 30 nm. The triple doped samples showed multicolor emission on single wavelength excitation. The photoluminescence results were correlated with the lifetime data to get an insight into the luminescence and energy transfer processes taking place in the system. On excitation at 247 nm, the novel nanocrystalline Gd(2)O(3):RE (RE = Dy, Tb) phosphor resulted in having very impressive CIE chromaticity coordinates of x = 0.315 and y = 0.316, and a correlated color temperature of 6508 K, which is very close to standard daylight.

Nanocrystalline YCrO3 powder was synthesized by a combustion technique using glycine as the fuel and the corresponding metal nitrates as oxidants. Three different oxidant-to-fuel ratios namely fuel-deficient, stoichiometric and fuel-excess ratios were chosen to explore the possibility to prepare single-phasic YCrO3. The crystallite size for the phase pure product after calcination at 600 °C was found to be 36 nm by x-ray line broadening. The agglomerate behaviour was investigated by light scattering studies. The TEM observations clearly highlight the pronounced crystallinity for YCrO3. A striking observation was the presence of onion-like layers in HR-TEM micrographs. Magnetic measurements reveal the weak ferromagnetic nature of YCrO3 nanoparticles, although the bulk YCrO3 is reported to be an antiferromagnetic material.

No abstract

No abstract

Highly sinter-active powders of RE2O3 [rare earth (RE) = Gd, Eu, Dy] have been prepared using the corresponding metal nitrates as the oxidants, and glycine and citric acid as the fuels. Two different oxidant-to-fuel ratios, namely stoichiometric ratio and fuel-deficient ratio were used to explore the possibility of preparing different crystallographic modifications. By a careful control of oxidant-to-fuel ratio, nanocrystalline Eu2O3 and Gd2O3 could be prepared in cubic (C-type) as well as monoclinic (B-type) modifications. However, the high-temperature monoclinic modification could not be obtained for Dy2O3 due to a very high C-to-B-type phase transition temperature. The crystallite size, surface area, and sintering behavior were also studied for powders prepared using different oxidant-to-fuel ratios, and the results showed a remarkable correlation between different fuel contents and powder properties. Some of these powders resulted in pellets of nearly theoretical density. The sintered microstructure was studied by scanning electron microscopy.