Ultra-high performance (UHP) concrete is a special type of fibrous cementitious composite that is characterized by high strength and superior ductility, toughness, and durability. This research aimed to investigate the resistance of ultra-high performance fiber-reinforced concrete (UHPFRC) against repeated impacts. An adjusted repeated drop mass impact test was adopted to evaluate the impact performance of 72 UHPFRC disc specimens. The specimens were divided into six mixtures each of 12 discs. The only difference between the mixtures was the types of fibers used, while all other mixture components were the same. Three types of fibers were used: 6 mm micro-steel, 15 mm micro-steel, and polypropylene. All mixtures included 2.5% volumetric content of fibers, however with different combinations of the three fiber types. The test results showed that the mixtures with the 15 mm micro-steel fiber absorbed a higher number of impact blows until cracking compared to other mixtures. The mixture with pure 2.5% of 15 mm micro-steel fiber exhibited the highest impact resistance, with percentage increases over the other mixtures ranging from 25 to 140%. In addition, the Weibull distribution was used to investigate the cracking impact resistance of UHP at different levels of reliability.

No abstract

Currently, metal–matrix composite materials are some of the most promising types of materials, and they combine the advantages of a metal matrix and reinforcing particles/fibres. Within the framework of this article, the high-temperature synthesis of metal–matrix composite materials based on the (Ni-Ti)-TiB2 system was studied. The selected approaches make it possible to obtain composite materials of various compositions without contamination and with a high degree of energy efficiency during production processes. Combustion processes in the samples of a 63.5 wt.% NiB + 36.5 wt.% Ti mixture and the phase composition and structure of the synthesis products were researched. It has been established that the synthesis process in the samples proceeds via the spin combustion mechanism. It has been shown that self-propagating high-temperature synthesis (SHS) powder particles have a composite structure and consist of a Ni-Ti matrix and TiB2 reinforcement inclusions that are uniformly distributed inside it. The inclusion size lies in the range between 0.1 and 4 µm, and the average particle size is 0.57 µm. The obtained metal-matrix composite materials can be used in additive manufacturing technologies as ligatures for heat-resistant alloys, as well as for the synthesis of composites using traditional methods of powder metallurgy.

This work presents results in the field of synthesis of new metal matrix composites with matrix NiTi and particles TiB 2 , and their use as additives to fabricate metal matrix composites based on the Inconel 625 alloy. NiTi-TB 2 powders were obtained using self-propagating high-temperature synthesis. Composite NiTi-TiB 2 particles were spheroidized on a high-frequency induction plasmatron. Composite NiTi-TB 2 particles were mixed with metallic Inconel 625 powder with particle sizes of 50-150 µm. We used direct laser deposition by means of mixture of powders to grow samples with different contents of ceramics in the metal matrix. The process of direct laser deposition during the experiment was investigated. We have determined the peculiarities of the formation of the structure in metal matrix composites with different contents of titanium diboride. We have demonstrated the possibility of using Direct Laser Deposition (DLD) for fabricating items from ceramic metal materials. We have determined promising fields of further research for the purpose of obtaining efficient metal matrix composites using additive manufacturing technologies.

The novelty of this work consists of obtaining original fundamental data on the laws of synthesis of new metal matrix composite materials for additive technologies. CrN + TiNi composites were obtained using the method of self-propagating high-temperature synthesis. In this work, analysis of the parameters of the synthesis of composite materials as well as their structure and phase composition were carried out. A scheme for the formation of a composite structure is established; it is shown that the phase composition is represented by 54.6 wt.% CrN and 45.4 wt.% TiNi. It was shown that composites based on the system are suitable for machines that make use of direct laser deposition to grow layers of materials. Sample structure and phase parameters were studied. It is shown that titanium nitride particles are uniformly distributed in the CrNi intermetallic matrix, the TiN particle size ranges from 0.3 to 9 μm and the average particle size is 2.8 μm. The results obtained indicate the possibility of synthesizing promising metal matrix composite materials for additive technologies. Such materials may have increased hardness, operating temperature and strength.