4is newly-formed highly-dispersed solid particles of inorganic salts, which possess high fire-suppression capacity. In addition, with regard to the climate changes on the planet, an acute problem now is the limitation of CO 2 emission as well as that of halons and other greenhouse gases into the atmosphere. Replacement of CO 2 and halons, which are currently used for extinguishing the A, B, C, E grades of fire, is an urgent task in need of the fastest solution because of their harmful effect on the planet's climate and ecology, as well as on the ozone layer.Thus, the relevance of this work is explained by the fact that the fire-fighting tools are lacking at present with high fire suppression efficiency, eco-friendly, cheap, easy to manufacture and operate, which can be used even for fire extinguishing in the areas of temporary presence of people and living organisms without apparent damage to them as a result of filling up the areas with the mentioned fire suppression substances. Analysis of scientific literature and the problem statementA fire extinguishing aerosol is obtained by burning AFM, which consist of an oxidant, as a rule KNO 3, KClO 4 4

Теоретично обґрунтовано та експериментально підтверджено можливість використання ударних хвиль та об'ємних вогнегасних речовин для попередження займання газових горючих середовищ. Встановлено, що запропонована комбінована система, забезпечує ефективне попередження займання -флегматизування газової н-гептаноповітряної суміші при одночасному зниженні концентрації аерозолю та газів СО 2 або N 2 до 4 разів порівняно з їх індивідуальними значеннями Ключові слова: гази флегматизатори, інгібітори горіння, аерозольне пожежогасіння, ударні хвилі, вогнегасний аерозоль Дата надходження рукопису 19.09.2017 Баланюк Володимир Мірчович, кандидат технічних наук, доцент, полковник служби цивільного захисту, Відділ ад'юнктури та докторантури, Львівський державний університет безпеки життєдіяльності, вул. Клепарівска, 35, м. Львів, Україна, 79007 E-mail: bagr33@ukr.net Ковалишин Василь Васильович, доктор технічних наук, професор, завідувач кафедри, кафедра пожежної тактики та аварійно-рятувальних робіт, Львівський державний університет безпеки життєдіяльності, вул. Клепарівска, 35, м. Львів, Україна, 79007

This paper reports the analysis of compositions for fire protection of wood that established that there are not enough data to explain and describe the process of fire protection and, accordingly, the fire-hazardous properties of wood, in order to protect people. The development and research of a set of properties of fire-resistant materials leads to the design of new types of such materials. The object of this study was a fire-protective two-component intumescent varnish for wood. The essence of the research is to determine the indicators of fire danger of wood, fire-protected by coatings, and the impact exerted on them by the formed heat-insulating layer of coke, making it possible to justify the effectiveness of the fire-retardant coating under the influence of temperature. The volume of fire-retardant and hydrophobic coating has been optimized, which ensures the lowest value of loss of mass by fire-protected wood during thermal action. Its lowest value was determined when using flame retardant in the volume of 589 g/m2 and a hydrophobic agent in the volume of 54 g/m2. When determining the combustibility of fire-resistant wood, it was established that the temperature of flue gases during tests was no more than 103 °C, the length of damage to the sample did not exceed 143 mm. At the same time, the weight loss did not exceed 19 g, and the independent burning of wood did not exceed 23 s. In addition, the wood withstood the surface effect of a heat flow of 35 kW/m2, while surface combustion did not occur, and the value of the coefficient of smoke formation was 432 m2/kg during the smoldering of the fire-proof sample. Unlike wood protection with fire-retardant swelling paint, the fireproof wood with two-component varnish, does not change color and refers to low combustibility materials; it is hard to ignite, dose not spread the flame by surface, with moderate smoke-forming ability. The practical significance is the fact that a certificate of conformity was issued based on the reported results. Thus, there are grounds to assert the possibility of directed adjustment of wood fire protection processes by using coatings that can form a protective layer on the surface of the material

No abstract

СПОСІБ ПІДШАРОВОГО ГАСІННЯ СПИРТІВ ВОГНЕГАСНИМ АЕРОЗОЛЕМ © В. М. Баланюк, Н. М. Козяр, А. В. Кравченко Результати отримані в роботі підтвердили можливість використання вогнегасних аерозолів на основі неорганічних солей калію для підшарового гасіння спиртів в резервуарах. У порівнянні з класичними способами, даний спосіб забезпечує ефективне та надійне гасіння полум'я, адже аерозоль подається підшарово з рідини в резервуарі що забезпечує повне проникнення аерозолю в зону горіння, чистоту та високу швидкість гасіння Ключові слова: вогнегасний аерозоль, інгібітори горіння, аерозольне пожежогасіння, підшарове гасіння Рекомендовано до публікації д-р техн. наук., професор Ковалишин В. В. Дата надходження рукопису 05.02.2019 Баланюк Володимир Мірчович, кандидат технічних наук, доцент, кафедра процесів горіння та загальної хімії, Львівський державний університет безпеки життєдіяльності, вул. Клепарівска, 35, м. Львів,