The reaction between [V(IV)OSO(4)] and the tetradentate N(2)O(2)-donor Schiff base ligand, N,N-bis(o-hydroxybenzaldehyde)phenylenediamine (sal-HBPD), obtained by the condensation of salicylaldehyde and o-phenylenediamine in a molar ratio of 2 : 1 respectively, resulted in the formation of [V(IV)O(sal-HBPD)]. The molecular structure of [V(IV)O(sal-HBPD)] was determined by single crystal X-ray diffraction, and confirmed the distorted square pyramidal geometry of the complex with the N(2)O(2) binding mode of the tetradentate ligand. The formation of the polymer-supported p[V(IV)O(sal-AHBPD)] proceeded via the nitrosation of sal-HBPD, followed by the reduction with hydrogen to form an amine group that was then linked to Merrifield beads followed by the reaction with [V(IV)OSO(4)]. XPS and EPR were used to confirm the presence of oxovanadium(IV) within the beads. The BET surface area and porosity of the heterogeneous catalyst p[V(IV)O(sal-AHBPD)] were found to be 6.9 m(2) g(-1) and 180.8 Å respectively. Microanalysis, TG, UV-Vis and FT-IR were used for further characterization of both [V(IV)O(sal-HBPD)] and p[V(IV)O(sal-AHBPD)]. Oxidation of dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) was investigated using [V(IV)O(sal-HBPD)] and p[V(IV)O(sal-AHBPD)] as catalysts. Progress for oxidation of these model compounds was monitored with a gas chromatograph fitted with a flame ionization detector. The oxidation products were characterized using gas chromatography-mass spectrometry, microanalysis and NMR. Dibenzothiophene sulfone (DBTO(2)) and 4,6-dimethyldibenzothiophene sulfone (4,6-DMDBTO(2)) were found to be the main products of oxidation. Oxovanadium(IV) Schiff base microspherical beads, p[V(IV)O(sal-AHBPD)], were able to catalyse the oxidation of sulfur in dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) to a tune of 88.0% and 71.8% respectively after 3 h at 40 °C. These oxidation results show promise for potential application of this catalyst in the oxidative desulfurization of crude oils.
Both polymer microspheres and microfibers containing the imidazole functionality have been prepared and used to immobilize oxovanadium(IV). The average diameters and BET surface areas of the microspheres were 322 mm and 155 m 2 g À1 while the fibers were 1.85 mm and 52 m 2 g À1 , respectively. XPS and microanalysis confirmed the incorporation of imidazole and vanadium in the polymeric materials. The catalytic activity of both materials was evaluated using the hydrogen peroxide facilitated oxidation of thioanisole. The microspheres were applied in a typical laboratory batch reactor set-up and quantitative conversions (>99%) were obtained in under 240 min with turn-over frequencies ranging from 21.89 to 265.53 h À1 , depending on the quantity of catalyst and temperature. The microspherical catalysts also proved to be recyclable with no drop in activity being observed after three successive reactions. The vanadium functionalized fibers were applied in a pseudo continuous flow set-up. Factors influencing the overall conversion and product selectivity, including flow rate and catalyst quantity, were investigated. At flow rates of 1-4 mL h À1 near quantitative conversion was maintained over an extended period. Keeping the mass of catalyst constant (0.025 g) and varying the flow rate from 1-6 mL h À1 resulted in a shift in the formation of the oxidation product methyl phenyl sulfone from 60.1 to 18.6%.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.