In this study, we prepared a homogeneous fine powder of barium titanate (BaTiO3, BT) doped with different concentrations of strontium (x = 0, 0.05, 0.125, 0.15, 0.20, and 0.3) and having the composition Ba1-xSrxTiO3 (barium strontium titanate, BSrxT). XRD patterns and Rietveld refinement revealed the existence of a single tetragonal phase structure for BSrxT, x = 0–20%, and a single cubic structure for BSr30%T. The physical properties of the pure and doped mixtures were studied. The results showed that the addition of strontium to the physical properties of BaTiO3, including the apparent porosity, bulk density, linear shrinkage, and water absorption have been changed when increasing the Sr content. Moreover, the inclusion of 15% Sr in BaTiO3 increases the apparent porosity and water absorption of the sample to 6.2 and 28.5%, respectively. The optical properties were investigated by Ultraviolet–visible spectroscopy and it was found that the optical band gap decreases significantly with increasing Sr concentration, from 3.10 for pure BaTiO3 to 2.46 eV for the BSr30%T compound. The thermal conductivity measurements showed that the doping mechanism and the increased temperature have a significant effect on the thermal conductivity results of the fabricated ceramic materials. Therefore, it was found that the value of thermal conductivity increases with increasing Sr doping and at higher temperatures. A correlated behavior of optimum values is observed in band gap energy, absorption, and thermal conductivity which can be exploited for thermo-optical applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.