Al-Fe hypoeutectic alloys are a family of casting alloys characterized by cell growth, low cost and appreciable formability. It is well known that fatigue strength is a requirement of prime importance considering the nature of load typically observed during operations involving the risers used in oil extraction. The aim of this study is to examine the influence of cell size and its intercellular phase distribution on the fatigue life (N f ) of the directionally solidified Al-0.5, 1.0 and 1.5wt% Fe alloys. A water-cooled vertical upward unidirectional solidification system was used to provide the castings. Microscopy light and SEM microscopy were used. It was found that fatigue life decreases as cell spacing (λ c ) increases. Smaller cell spacing allows a homogeneous distribution of Al-Fe fibers to happen within the intercellular regions, which tends to improve the mentioned fatigue property. ); where A and B are constants] seems to be able to encompass the fatigue life variation along the Al-Fe alloys.

Agradeço a todas as pessoas que contribuíram neste trabalho, especialmente: Ao amigo e orientador Prof. Dr. Hélio Goldenstein, pela solidariedade e convivência fraternal e pelas discussões diversas e teóricas, pela orientação democrática e pela confiança demonstrada. Ao inestimável Leandro A. da Silva pela colaboração dedicada e pela convivência fraternal. Ao Prof. Dr. Mário Boccalini Jr. pela colaboração e discussões e a seus colaboradores no IPT Dito, Almeida, Bispo e Robson, pela imprescindível contribuição na obtenção das ligas fundidas. Ao Prof. Dr. Arnaldo Andrade (IPEN) pelas discussões iniciais sobre tenacidade à fratura. Aos amigos Nonato, Estéfano e Zé Roberto pela solidariedade e convivência fraternal. A todos os colegas da pós-graduação do PMT/EPUSP pela convivência enriquecedora e permanente colaboração mútua. Ao Prof. Dr. Jorge Tenório (PMT/EPUSP) pela colaboração permanente. Aos funcionários do PMT/EPUSP Cléria, Cristina, Danilo, Lívio, Ivo e Rubens pela inestimável colaboração. Aos amigos e colaboradores Prof. Dr. João Telésforo (LFS/EPUSP; UFRN), Dr. Humberto Yoshimura (IPT) pela imprescindível contribuição na execução dos procedimentos experimentais e fundamentais discussões. Ao Isaac (IG/USP), Nildemar (IPEN), Eliana (PMI/EPUSP), Francisco e Eguiberto (PMT/EPUSP); Marilene e Prof. Dr. Nelson (IPEN) pela ajuda na caracterização dos materiais utilizados. Aos amigos Edson e Alexandra pela ajuda no fechamento do trabalho. À INA BRASIL pela concessão de amostras de aço DIN 100 Cr6, utilizadas nos experimentos preliminares; à Villares Metals pela concessão de amostras dos aços AISI M2 e SINTER 23, utilizados nos experimentos preliminares e nas comparações das propriedades dos aços fundidos e modificados; À CAPES, pela concessão da bolsa de mestrado, à FAPESP, pela concessão do auxílio à pesquisa (processo 98/14.770-0) que viabilizaram a realização deste trabalho, ao LFS/Villares Cilindros por concessão de bolsa.