The unusual property of negative thermal expansion is of fundamental interest and may be used to fabricate composites with zero or other controlled thermal expansion values. Here we report that colossal negative thermal expansion (defined as linear expansion <−10−4 K−1 over a temperature range ~100 K) is accessible in perovskite oxides showing charge-transfer transitions. BiNiO3 shows a 2.6% volume reduction under pressure due to a Bi/Ni charge transfer that is shifted to ambient pressure through lanthanum substitution for Bi. Changing proportions of coexisting low- and high-temperature phases leads to smooth volume shrinkage on heating. The crystallographic linear expansion coefficient for Bi0.95La0.05NiO3 is −137×10−6 K−1 and a value of −82×10−6 K−1 is observed between 320 and 380 K from a dilatometric measurement on a ceramic pellet. Colossal negative thermal expansion materials operating at ambient conditions may also be accessible through metal-insulator transitions driven by other phenomena such as ferroelectric orders.

The structural and electronic properties of BiCoO(3) under high pressure have been investigated. Synchrotron X-ray and neutron powder diffraction studies show that the structure changes from a polar PbTiO(3) type to a centrosymmetric GdFeO(3) type above 3 GPa with a large volume decrease of 13% at room temperature revealing a spin-state change. The first-order transition is accompanied by a drop of electrical resistivity. Structural results show that Co(3+) is present in the low spin state at high pressures, but X-ray emission spectra suggest that the intermediate spin state is present. The pressure-temperature phase diagram of BiCoO(3) has been constructed enabling the transition temperature at ambient pressure to be estimated as 800-900 K.