The ability to protect refined metals from reactive environments is vital to many industrial and academic applications. Current solutions, however, typically introduce several negative effects, including increased thickness and changes in the metal physical properties. In this paper, we demonstrate for the first time the ability of graphene films grown by chemical vapor deposition to protect the surface of the metallic growth substrates of Cu and Cu/Ni alloy from air oxidation. In particular, graphene prevents the formation of any oxide on the protected metal surfaces, thus allowing pure metal surfaces only one atom away from reactive environments. SEM, Raman spectroscopy, and XPS studies show that the metal surface is well protected from oxidation even after heating at 200 °C in air for up to 4 h. Our work further shows that graphene provides effective resistance against hydrogen peroxide. This protection method offers significant advantages and can be used on any metal that catalyzes graphene growth.

No abstract

Using micro-Raman spectroscopy, the thermal conductivity of a graphene monolayer grown by chemical vapor deposition and suspended over holes with different diameters ranging from 2.9 to 9.7 μm was measured in vacuum, thereby eliminating errors caused by heat loss to the surrounding gas. The obtained thermal conductivity values of the suspended graphene range from (2.6 ± 0.9) to (3.1 ± 1.0) × 10(3) Wm(-1)K(-1) near 350 K without showing the sample size dependence predicted for suspended, clean, and flat graphene crystal. The lack of sample size dependence is attributed to the relatively large measurement uncertainty as well as grain boundaries, wrinkles, defects, or polymeric residue that are possibly present in the measured samples. Moreover, from Raman measurements performed in air and CO(2) gas environments near atmospheric pressure, the heat transfer coefficient for air and CO(2) was determined and found to be (2.9 +5.1/-2.9) and (1.5 +4.2/-1.5) × 10(4) Wm(-2)K(-1), respectively, when the graphene temperature was heated by the Raman laser to about 510 K.