Uniform and extremely small-sized iron oxide nanoparticles (ESIONs) of < 4 nm were synthesized via the thermal decomposition of iron-oleate complex in the presence of oleyl alcohol. Oleyl alcohol lowered the reaction temperature by reducing iron-oleate complex, resulting in the production of small-sized nanoparticles. XRD pattern of 3 nm-sized nanoparticles revealed maghemite crystal structure. These nanoparticles exhibited very low magnetization derived from the spin-canting effect. The hydrophobic nanoparticles can be easily transformed to water-dispersible and biocompatible nanoparticles by capping with the poly(ethylene glycol)-derivatized phosphine oxide (PO-PEG) ligands. Toxic response was not observed with Fe concentration up to 100 μg/mL in MTT cell proliferation assay of POPEG-capped 3 nm-sized iron oxide nanoparticles. The 3 nm-sized nanoparticles exhibited a high r(1) relaxivity of 4.78 mM(-1) s(-1) and low r(2)/r(1) ratio of 6.12, demonstrating that ESIONs can be efficient T(1) contrast agents. The high r(1) relaxivities of ESIONs can be attributed to the large number of surface Fe(3+) ions with 5 unpaired valence electrons. In the in vivo T(1)-weighted magnetic resonance imaging (MRI), ESIONs showed longer circulation time than the clinically used gadolinium complex-based contrast agent, enabling high-resolution imaging. High-resolution blood pool MR imaging using ESIONs enabled clear observation of various blood vessels with sizes down to 0.2 mm. These results demonstrate the potential of ESIONs as T(1) MRI contrast agents in clinical settings.

No abstract

Highly versatile nanocomposite nanoparticles were synthesized by decorating the surface of mesoporous dye-doped silica nanoparticles with multiple magnetite nanocrystals. The superparamagnetic property of the magnetite nanocrystals enabled the nanoparticles to be used as a contrast agent in magnetic resonance (MR) imaging, and the dye molecule in the silica framework imparted optical imaging modality. Integrating a multitude of magnetite nanocrystals on the silica surface resulted in remarkable enhancement of MR signal due to the synergistic magnetism. An anticancer drug, doxorubicin (DOX), could be loaded in the pores and induced efficient cell death. In vivo passive targeting and accumulation of the nanoparticles at the tumor sites was confirmed by both T2 MR and fluorescence imaging. Furthermore, apoptotic morphology was clearly detected in tumor tissues of mice treated with DOX loaded nanocomposite nanoparticles, demonstrating that DOX was successfully delivered to the tumor sites and its anticancer activity was retained.

No abstract

The theoretically predicted maximum r(2) relaxivity of iron oxide nanoparticles was achieved by optimizing the overall size of ferrimagnetic iron oxide nanocubes. Uniform-sized iron oxide nanocubes with an edge length of 22 nm, encapsulated with PEG-phospholipids (WFION), exhibited high colloidal stability in aqueous media. In addition, WFIONs are biocompatible and did not affect cell viability at concentrations up to 0.75 mg Fe/ml. Owing to the enhanced colloidal stability and the high r(2) relaxivity (761 mM(-1) s(-1)), it was possible to successfully perform in vivo MR imaging of tumors by intravenous injection of 22-nm-sized WFIONs, using a clinical 3-T MR scanner.