The purpose of this study was to demonstrate the feasibility of using a fibrin glue polymer to produce injectable tissue-engineered cartilage and to determine the optimal fibrinogen and chondrocyte concentrations required to produce solid, homogeneous cartilage. The most favorable fibrinogen concentration was determined by measuring the rate of degradation of fibrin glue using varying concentrations of purified porcine fibrinogen. The fibrinogen was mixed with thrombin (50 U/cc in 40 mM calcium chloride) to produce fibrin glue. Swine chondrocytes were then suspended in the fibrinogen before the addition of thrombin. The chondrocyte/polymer constructs were injected into the subcutaneous tissue of nude mice using chondrocyte concentrations of 10, 25, and 40 million chondrocytes/cc of polymer (0.4-cc injections). At 6 and 12 weeks, the neocartilage was harvested and analyzed by histology, mass, glycosaminoglycan content, DNA content, and collagen type II content. Control groups consisted of nude mice injected with fibrin glue alone (without chondrocytes) and a separate group injected with chondrocytes suspended in saline only (40 million cells/cc in saline; 0.4-cc injections). The fibrinogen concentration with the most favorable rate of degradation was 80 mg/cc. Histologic analysis of the neocartilage showed solid, homogeneous cartilage when using 40 million chondrocytes/cc, both at 6 and 12 weeks. The 10 and 25 million chondrocytes/cc samples showed areas of cartilage separated by areas of remnant fibrin glue. The mass of the samples ranged from 0.07 to 0.12 g at 6 weeks and decreased only slightly by week 12. The glycosaminoglycan content ranged from 2.3 to 9.4 percent for all samples; normal cartilage controls had a content of 7.0 percent. DNA content ranged from 0.63 to 1.4 percent for all samples, with normal pig cartilage having a mean DNA content of 0.285 percent. The samples of fibrin glue alone produced no cartilage, and the chondrocytes alone produced neocartilage samples with a significantly smaller mass (0.47 g at 6 weeks and 0.46 g at 12 weeks) when compared with all samples produced from chondrocytes suspended in fibrin glue (p < 0.03). Gel electrophoreses demonstrated the presence of type II collagen in all sample groups. This study demonstrates that fibrin glue is a suitable polymer for the formation of injectable tissue-engineered cartilage in the nude mouse model. Forty million chondrocytes per cc yielded the best quality cartilage at 6 and 12 weeks when analyzed by histology and content of DNA, glycosaminoglycan, and type II collagen.

The purpose of this study was to determine if chondrocytes cultured through several subcultures at very low plating density would produce new cartilage matrix after being reimplanted in vivo with or without a hydrogel polymer scaffold. Chondrocytes were initially plated in low-density monolayer culture, grown to confluence, and passaged four times. After each passage cells were suspended in purified porcine fibrinogen and injected into the subcutaneous space of nude mice while simultaneously polymerizing with thrombin to reach a final concentration of 40 million cells/cc. Controls were made by injecting fresh, uncultured cells with fibrin polymer and by injecting the cultured cells in saline (without polymer). All samples were harvested at 6 weeks. When injected in polymer, both fresh cells and cells that had undergone only one passage in culture produced cartilaginous nodules. Cultured cells did not produce cartilage, regardless of length of time spent in culture, when injected without polymer. Cartilage was also not recovered from samples with cells kept in culture for longer than one passage, even when provided with a polymer matrix. All samples harvested were subjected to histological analysis and assayed for total DNA, glycosaminoglycan (GAG), and type II collagen. There was histological evidence of cartilage in the groups that used fresh cells and cultured cells suspended in fibrin polymer that only underwent one passage. No other group contained areas that would be consistent with cartilage histologically. All experimental samples had a higher percent of DNA than native swine cartilage, and there was no statistical difference between the DNA content of the groups containing cultured or fresh cells in fibrin polymer. Whereas the GAG content of native cartilage was 8.39% of dry weight and fresh cells in fibrin polymer was 12.85%, cultured cells in fibrin polymer never exceded the 2.48% noted from first passage cells. In conclusion, this study demonstrates that porcine chondrocytes that have been cultured in monolayer for one passage will produce cartilage in vivo when suspended in fibrin polymer.

The purpose of this study was to determine whether or not a synthetic photopolymerized tissue adhesive (polyethylene oxide hydrogel) is useful in seroma prevention using a well established rat mastectomy seroma model. Twenty-three Sprague-Dawley rats received mastectomies. The rats were randomly assigned to either the control group (n = 13) or the experimental group (n = 10). The control animals received 0.2 cc of saline into the wound before closure. The experimental group received either 0.2 cc (n = 5) or 0.4 cc (n = 5) of the polyethylene oxide polymer into their wounds before closure. The experimental animals were placed under an ultraviolet A lamp for 3 minutes to polymerize the adhesive. On postoperative day seven, the resultant seromas were quantified, and wound tissues were harvested for histologic evaluation. The rats in the control group had a mean seroma volume of 3.25 cc (SD = 2.41), whereas the rats treated with polymer had a mean seroma volume of 0.37 cc (SD = 0.51). A Student's t test was performed showing a statistically significant difference between the control and experimental groups (p < 0.005). The volume of polymer used (0.2 cc versus 0.4 cc) did not significantly impact the volume of the resultant seromas. This study demonstrates that photopolymerizable polyethylene oxide hydrogels can be used as a tissue adhesive and that such an adhesive significantly reduces seroma formation in the rat mastectomy model.