Streptococcus agalactiae and Staphylococcus aureus are two pathogenetic agents of several infective diseases in humans. Biocidal effects and cellular internalization of ZnO nanoparticles (NPs) on two bacteria are reported, and ZnO NPs have a good bacteriostasis effect. ZnO NPs were synthesized in the EG aqueous system through the hydrolysis of ionic Zn2+ salts. Particle size and shape were controlled by the addition of the various surfactants. Bactericidal tests were performed in an ordinary broth medium on solid agar plates and in liquid systems with different concentrations of ZnO NPs. The biocidal action of ZnO materials was studied by transmission electron microscopy of bacteria ultrathin sections. The results confirmed that bactericidal cells were damaged after ZnO NPs contacted with them, showing both gram-negative membrane and gram-positive membrane disorganization. The surface modification of ZnO NPs causes an increase in membrane permeability and the cellular internalization of these NPs whereas there is a ZnO NP structure change inside the cells.
In this paper, a hierarchical NiCo2S4@polypyrrole core-shell heterostructure nanotube array on Ni foam (NiCo2S4@PPy/NF) was successfully developed as a bind-free electrode for supercapacitors. NiCo2S4@PPy-50/NF obtained under 50 s PPy electrodeposition shows a low charge-transfer resistance (0.31 Ω) and a high area specific capacitance of 9.781 F/cm(2) at a current density of 5 mA/cm(2), which is two times higher than that of pristine NiCo2S4/NF (4.255 F/cm(2)). Furthermore, an asymmetric supercapacitor was assembled using NiCo2S4@PPy-50/NF as positive electrode and activated carbon (AC) as negative electrode. The resulting NiCo2S4@PPy-50/NF//AC device exhibits a high energy density of 34.62 Wh/kg at a power density of 120.19 W/kg with good cycling performance (80.64% of the initial capacitance retention at 50 mA/cm(2) over 2500 cycles). The superior electrochemical performance can be attributed to the combined contribution of both component and unique core-shell heterostructure. The results demonstrate that the NiCo2S4@PPy-50 core-shell heterostructure nanotube array is promising as electrode material for supercapacitors in energy storage.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.