Well-defined (nearly monodispersed) poly(poly(ethylene glycol)monomethacrylate)-Si hybrids were prepared via surface-initiated atom transfer radical polymerization (ATRP) of the poly(ethylene glycol)monomethacrylate (PEGMA) macromonomer on the hydrogen-terminated Si(111) surface (Si-H surface). Both the active chloride groups at the chain ends (from the ATRP process) and the chloride groups converted from some ( approximately 32%) of the -OH groups of the Si-C bonded PEGMA polymer, or P(PEGMA), brushes were used as leaving groups for the covalent coupling of heparin. For the heparinized P(PEGMA)-Si hybrid surfaces, protein adsorption and platelet adhesion were significantly suppressed. The well-defined and dense P(PEGMA) brushes, prepared from surface-initiated ATRP, had allowed the immobilization of a relatively high concentration of heparin (about 14 mug/cm(2)). The resulting silicon surface exhibited significantly improved antithrombogenecity with a plasma recalcification time (PRT) of about 150 min. The persistence of high bioactivity for the immobilized heparin on the hybrid surfaces can be attributed to the biocompatibility of the PEGMA units, as well as their role as spacers in providing the immobilized heparin with a higher degree of conformational freedom in a more hydrophilic environment. Thus, the heparin-coupled P(PEGMA)-Si hybrids with anti-fouling and antithrombogenic surfaces are potentially useful in silicon-based implantable devices and tissue engineering.

A simple one-step procedure was employed for the covalent immobilization of an atom-transfer radical polymerization (ATRP) initiator, via the robust Si-C bond, on the hydrogen-terminated Si(111) surface (Si-H surface). Well-defined poly(glycidyl methacrylate) [P(GMA)] brushes, tethered directly on the (111)-oriented single-crystal silicon surface, were prepared via surface-initiated ATRP. Kinetics study on the surface-initiated ATRP of glycidyl methacrylate revealed that the chain growth from the silicon surface was consistent with a "controlled" process. A relatively high concentration of glucose oxidase (GOD; above 0.2 mg/cm2) could be coupled directly to the well-defined P(GMA) brushes via the ring-opening reaction of the epoxide groups with the amine moieties of the enzyme. The resultant GOD-functionalized P(GMA) brushes, with the accompanying hydroxyl groups from the ring-opening reaction of the epoxide groups, serves as an effective spacer to provide the GOD with a higher degree of conformational freedom and a more hydrophilic environment. An equivalent enzyme activity above 1.6 units/cm2 [micromoles of beta-D-(+)-glucose oxidized to d-gluconolactone per minute per square centimeter] and a corresponding relative activity of about 60% could be readily achieved. The immobilized GOD also exhibited an improved stability during storage over that of the free enzyme. The GOD-functionalized silicon substrates are potentially useful to the development of silicon-based glucose biosensors.

Linear, branched, and arborescent fluoropolymer-Si hybrids were prepared via surface-initiated atom transfer radical polymerization (ATRP) from the 4-vinylbenzyl chloride (VBC) inimer and ClSO(3)H-modified VBC that were immobilized on hydrogen-terminated Si(100), or Si-H, surfaces. The simple approach of UV-induced coupling of VBC with the Si-H surface provided a stable, Si-C bonded monolayer of "monofunctional" ATRP initiators (the Si-VBC surface). The aromatic rings of the Si-VBC surface were then sulfonated by ClSO(3)H to introduce sulfonyl chloride (-SO(2)Cl) groups and to give rise to a monolayer of "bifunctional" ATRP initiators. Kinetics study indicated that the chain growth of poly(pentafluorostyrene) from the functionalized silicon surfaces was consistent with a "controlled" or "living" process. The chemical composition and functionality of the silicon surface were tailored by the well-defined linear and branched fluoropolymer brushes. Atomic force microscopy images revealed that the surface-initiated ATRP of pentafluorostyrene (PFS) had proceeded uniformly on the Si-VBC surface to give rise to a dense and molecularly flat surface coverage of the linear brushes. The uniformity of surfaces with branched brushes was controlled by varying the feed ratio of the monomer and inimer (VBC in the present case). The living chain ends on the functionalized silicon surfaces were used as the macroinitiators for the synthesis of diblock copolymer brushes, consisting of the PFS and methyl methacrylate polymer blocks.

The ability to manipulate and control the surface properties of nylons is of crucial importance to their widespread applications. In this work, surface-initiated atom-transfer radical polymerization (ATRP) is employed to tailor the functionality of the nylon membrane and pore surfaces in a well-controlled manner. A simple two-step method, involving the activation of surface amide groups with formaldehyde and the reaction of the resulting N-methylol polyamide with 2-bromoisobutyryl bromide, was first developed for the covalent immobilization of ATRP initiators on the nylon membrane and its pore surfaces. Functional polymer brushes of 2-hydroxyethyl methacrylate (HEMA) and poly(ethylene glycol)monomethacrylate (PEGMA) were prepared via surface-initiated ATRP from the nylon membranes. A kinetics study revealed that the chain growth from the membranes was consistent with a "controlled" process. The dormant chain ends of the grafted HEMA polymer (P(HEMA)) and PEGMA polymer (P(PEGMA)) on the nylon membranes could be reactivated for the consecutive surface-initiated ATRP to produce the corresponding nylon membranes functionalized by P(HEMA)-b-P(PEGMA) and P(PEGMA)-b-P(HEMA) diblock copolymer brushes. In addition, membranes with grafted P(HEMA) and P(PEGMA) brushes exhibited good resistance to protein adsorption and fouling under continuous-flow conditions.

The halogen-terminated Si(111) (Si-X, X = Cl, Br) surfaces contain effective initiators for surface-initiated atom transfer radical polymerization. Well-defined polymer-Si hybrids, consisting of covalently tethered (Si-C bonded) functional polymer brushes, can be prepared directly from the Si-X surfaces.