Latex based on fluoroacrylate (TAN) and other comonomers was prepared via miniemulsion polymerization in the presence of stearyl trimethyl ammonium chloride (STAC) and 2, 2Ј-azobis (2-amidinopropane) dihydrochloride (ABAP) as a water soluble initiator. Light transmittance studies demonstrated that the light transmittance of prepared emulsions increases with the amount of TAN, STAC, cosolvent DPM, and hydrophobe DM. Given suitable reaction temperature and quantities of TAN, STAC, DPM, and DM, a copolymer emulsion of fluoroacylate with a particle size of 50 nm was produced. The water repellency tested on polyester fabrics displayed greater effectiveness than that of commercial products with higher fluorine content.
ABSTRACT:The fluorinated copolymer emulsions containing different monomers with the reactive groups were successfully prepared at our lab, using emulsion polymerization technique. The water repellency and the durability for the fabrics treated by fluorinated water repellents after 30 and 50 washes were measured and compared. Actually, the combination of the comonomers containing blocked isocyanate or other reactive groups after copolymerization would increase the durability of the water repellency. In addition, the blocked isocyanate crosslinking agent (Jintexguard FCN) does, indeed, substantially increase the durability also. It clearly indicates that the copolymer emulsion prepared by the reaction of fluorinated acrylate, cyclohexyl methacrylate, and 3-chloro-2-hydroxy-propyl methacrylate(Topolene M) with monomers containing blocked isocyanate group(Jintexan BIA) showed very good durability. More importantly, the combination of this copolymer and Jintexguard FCN will significantly provide excellent water repellency and durability after 50 washes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.