After different rolling conditions, four 7055 aluminum alloy samples with different precipitation sizes were measured by scanning electron microscope, transmission electron microscope and laser ultrasonic. The attenuation coefficients of ultrasound measured by laser ultrasonic were calculated in the time domain, frequency domain and wavelet denoising, respectively. The relationship between the precipitate size and attenuation coefficient was established. The results show that the attenuation of the ultrasonic wave is related to the size of the precipitated phase; this provides a new method for rapid non-destructive testing of the precipitation of aluminum alloys.

Multi-pulse nanosecond laser ablation of Ti–6Al–4V is a complex process. In this study, the effect of substrate temperature on the nanosecond laser ablation of Ti–6Al–4V was investigated. Morphology, diameter and depth of ablation craters were observed; ablation efficiency ω (μm3/mJ) was proposed to analyzes the ablation process. The results showed that, with the increasing of substrate temperature, the ablation craters’ diameter increased and depth decreased, while ω initially increased, but then decreased rapidly. Furthermore, with increasing pulse number, the depth of ablation crater increased linearly, while the growth of the diameter gradually slowed down and tended to be stable after the 16th irradiation. The above changes were different in details at different substrate temperatures.