In recent decades, several studies have considered the use of plastic waste as a partial substitute for aggregate in green concrete. Such concrete has been limited to non-structural applications due to its low strength. This raises whether such concrete can be enhanced for use in some structural applications. This paper reports an attempt to develop a structural-grade concrete containing plastic waste aggregate with high proportions of substitution and confined with carbon fiber reinforced polymer (CFRP) fabrics. Experimental research was conducted involving the casting and testing 54 plain and confined concrete cylinders. A concrete mixture was designed in which the fine aggregate was partially replaced by polyethylene terephthalate (PET) waste plastic at ratios of 0%, 25%, and 50%, and with different w/c ratios of 0.40, 0.45, and 0.55. The results show that confinement has a substantial positive effect on the compressive behavior of PET concrete. The enhancement efficiency increases by 8–190%, with higher enhancement levels for higher substitution ratios. Adding one layer of CFRP fabric raises the ultimate strength of samples that have lost compressive strength to a level close to that of unconfined samples not containing PET. This confinement is accompanied by an increase in the slope of the stress-strain curve and greater axial and lateral strain values at failure. For the specimens confined by CFRP fabric, PET aggregate can be used as a partial substitute for sand at a replacement ratio of up to 50% by volume for structural applications. This paper also considers the ability of existing models to predict the strength of confined-PET concrete circular cross-sections by comparing model predictions with experimental results. The strength of confined PET concrete elements can’t be accurately predicted by any of the models that are already out there. It’s important to come up with a new model for these elements.

No abstract

In this study, PET plastic waste, which is a type of polymer commonly used in the manufacture of plastic bottles, has been incorporated into concrete by partially replacing the natural fine aggregate. An experimental study was conducted by casting and testing 90 concrete cylinders and 54 concrete cubes. A concrete mixture was designed in which the natural fine aggregate was substituted partially with PET plastic waste (PW) at a ratio of 0%, 25%, and 50%, with various w/c ratios of .40, .45, and .55. Physical, mechanical, and durability properties were assessed. The downside of the test results show degradation in each of the following characteristics: slump, compressive strength, splitting tensile strength, ultrasonic pulse velocity, water absorption, and porosity. The degradation of these characteristics increased with the increase in the volume of plastic aggregate (PA) and the w/c ratio. While the positive side of the results showed that with the increase of the PA volume and the w/c ratio, the fresh and dry densities decreased further, and by using 50% PET, the dry density became below 2000 kg/m3. Therefore, it is classified as lightweight concrete. Moreover, the fracture of concrete changed from brittle to more ductile compared to control concrete. Also, the thermal conductivity decreased significantly (11%–47%), and by using 50% of PET, the thermal conductivity became less than .71 W/mK, and accordingly, classified as a bearing insulator.

No abstract