Here, a Sn–C composite material prepared from bulk precursors (tin metal, graphite, and melamine) using ball milling and annealing is reported. The composite (58 wt% Sn and 42 wt% N‐doped carbon) shows a capacity up to 445 mAh gSn+C−1 and an excellent cycle life (1000 cycles). For the graphite, the ball milling leads to graphene nanoplatelets (GnP) for which the storage mechanism changes from solvent co‐intercalation to conventional intercalation. The final composite (Sn at nitrogen‐doped graphite nanoplatelets (SnNGnP)) is obtained by combining the GnPs with Sn and melamine as the nitrogen source. Rate‐dependent measurements and in situ X‐ray diffraction are used to study the asymmetric storage behavior of Sn, which shows a more sloping potential profile during sodiation and more defined steps during desodiation. The disappearance of two redox plateaus during desodiation is linked to the preceding sodiation current density (memory effect). The asymmetric behavior is also found by in situ electrochemical dilatometry. This method also shows that the effective electrode expansion during sodiation is much smaller (about +14%) compared to what is expected from Sn (+420%), which gives a reasonable explanation for the excellent cycle life for the SnNGnP (and likely other nanocomposites in general). Next to the advantages, challenges, which result from the nanocomposite approach, are also discussed.
Preparation of heteroatom-functionalized porous carbon derived from byproducts of bean curd stick manufacture as an electrode material for high performance supercapacitors.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.