Continuous carbon fiber reinforced poly‐ether–ether–ketone (CCF/PEEK) shows great potential in engineering applications attributed to superior mechanical properties together with excellent thermal and chemical resistance. In this study, a laser‐assisted additive manufacturing device was established to accurately collect and control the preheating temperature based on a coaxial infrared temperature measurement system. The influence on laser power consumption, interlaminar shear performance, and failure mechanism was investigated in condition of different preheating temperatures and printing speeds. Results indicated that the laser‐preheated specimens showed much higher ILSS with maximum values and increasing percentage reached 33.48 MPa and 157.0% compared to unpretreated specimens. With the increase of preheating temperature and printing speed, more laser power was consumed, while the ILSS and increasing percentage increased firstly and then decreased. The strengthening effect on the interlayer bonding was ascribed to promoting the penetration of PEEK molecular chain ends between adjacent layers, increasing the fluidity and enhancing the bonding effect between adjacent filament together with improving the impregnation behavior of the inner fibers. The proposed interlaminar strengthening method based on laser‐assisted preheating provides potential application prospects in aerospace and automotive industries.

Nanocrystalline deformed layers were generated in cadmium zinc telluride (CZT) single crystals by nanogrinding using three different grit sizes. The mechanical properties of the deformed layers were measured using nanoindentation. The hardness of the deformed nanocrystalline layers in the soft-brittle CZT semiconductor was higher than that of the perfect single crystal. This result is different from those found for deformed layers of hard-brittle silicon semiconductors, where the hardness of the deformed layers is lower than those of the perfect single crystal.