To improve the flexural properties of cemented soils reinforced with fibers and avoid their brittle failure when subjected to complex loading conditions, a simple and cost-effective technique was explored to facilitate their application in retaining walls. In this study, how different fiber surface modifications, i.e., alkali treatment, acid treatment and silane coupling agent treatment, as well as different fiber contents, i.e., 0%, 0.25%, 0.5% and 1%, affect the bending properties of cemented soils was investigated by conducting three-point bending tests on notched beams. The digital image correlation (DIC) technology was used to examine the crack propagation process and the strain field distribution of cracks in specimens in the flexural tests. The results show that all fiber surface modifications increased peak strength and fracture energy, for example, the fracture energy of specimens AN1, AH1 and AK1 was increased by 180.4%, 121.5% and 155.4%, respectively, compared to PVA1. In addition, the crack tip strain, crack propagation rate and the initial crack width of the modified specimens were lower than those before modification. Lastly, scanning electron microscope (SEM) and mercury intrusion porosimetry tests were adopted to reveal the mechanism of bending performance in cemented soils reinforced by fiber surface modifications.

Desiccation cracking frequently occurs in mud, clay, and pavement. Understanding the evolution of desiccation cracking may facilitate the development of techniques to mitigate cracking and even prevent it from developing altogether. In this study, experimental investigations were performed focusing on the effects of fibers on the evolution of desiccation cracking in soil-cement. Varied types of fibers (i.e., jute fiber and polyvinyl alcohol fiber (PVA)) and fiber contents (i.e., 0%, 0.25%, 0.5%, and 1%) were involved. The digital image correlation (DIC) method was employed to capture the evolution and propagation of cracks in the soil-cement specimens when subjected to desiccation. The results show that the presence of fibers imposes significant effects on the crack propagation pattern as well as the area and length of the cracks in the soil-cement during shrinkage. The addition of fibers, however, insignificantly affects the evaporation rate of the specimens. The crack area and crack length of the specimens decreased significantly when more fibers were included. There were no macroscopic cracks observed in the specimens where the fiber content was 1%. The DIC method effectively helped to determine the evolution of displacement and strain field on the specimens’ surface during the drying process. The DIC method is therefore useful for crack monitoring.