No abstract

Recebido em 19/7/06; aceito em 9/3/07; publicado na web em 24/7/07 STUDY OF THE PROPERTIES AND BIODEGRADABILITY OF POLYESTER/STARCH BLENDS SUBMITTED TO MICROBIAL ATTACK. This work deals with the biodegradation of blends of poly(β-hydroxybutyrate)/starch and poly(β-hydroxybutyrate-cohydroxyvalerate)/starch. The blends were obtained by evaporation of the solvent in the mixture of the polymers in chloroform. Tests were carried out in presence of micro-organisms which acted as biodegradation agents. The blends were consumed as carbon substrate and the production of CO 2 was evaluated in the process. In addition, the polyesters' mechanical properties were reduced by the incorporation of starch in its structure.( 1 H) NMR and infrared spectroscopy detected some characteristic polyester degradation groups in the polyesters' chemical structure, thus confirming the alteration suffered by it.Keywords: biodegradation; fungi; blends. INTRODUÇÃOO desenvolvimento na segunda metade do século XX foi profundamente marcado pelo surgimento dos materiais poliméricos e plásticos, os quais constituem atualmente boa parte dos materiais utilizados pelo homem.Os plásticos têm papel fundamental na sociedade moderna, mas devido ao fato de algumas aplicações destes materiais serem de descartabilidade muito rápida, associado à grande dificuldade de degradação no ambiente, podendo demorar séculos para se degradar e ocupando grande volume na área dos aterros, têm despertado fortes preocupações nos dias atuais [1][2][3][4][5][6][7] . O aumento no interesse científico pela área ambiental, atraído pelo crescimento explosivo do consumo de polímeros ou plásticos e pela disposição final destes resíduos sólidos urbanos, tem tornado cada vez mais necessária, a produção de substitutos ambientalmente sustentáveis, importantes no gerenciamento de resíduos, os chamados polímeros ou plásticos ambientalmente degradáveis (PADs), compostos por um vasto grupo de materiais poliméricos, naturais e sintéticos, que sofrem alterações químicas sob a influência de fatores ambientais 8 . Devido à preocupação mundial em não agredir o meio ambiente, um tipo de material polimérico vem merecendo atenção, os polidroxialcanoatos, principalmente o poli(β-hidroxibutirato) -PHB e seu copolímero poli(hidroxibutirato-co-valerato)-PHB-HV. A produção desses biopolímeros em grande escala acontece por um processo de fermentação bacteriana, sendo ainda um processo relativamente caro 9,10 . As blendas poliméricas usando o amido, em mistura com os polímeros biodegradáveis e polímero sintético, surgem como uma boa alternativa para minimizar os custos dos polímeros biodegradáveis, bem como aumentar a biodegradação dos polímeros sintéticos. Além disso, o amido é um material de baixo custo com valor estimado de US$ 0,50/kg 11 , sendo uma matéria-prima abundante que permite o desenvolvimento de produtos recicláveis e quando biodegradado ou incinerado libera CO 2 para a atmosfera 12 . Acredita-se que a mistura do plástico convencional com o polímero biodegradável possa resultar em um materi...

No abstract

Due to its ester bonds, poly(lactic acid) (PLA) undergoes biodegradation in humid environments, attracting market attention. The goal of this work was to observe the biodegradation in garden soil of PLA nanocomposites with neat (PLA/CNW) and surfactant modified cellulose nanowhiskers (PLA/ CNW/S). Three types of surfactants were tested: poly(ethylene glycol) monooleate (PEGMONO) and poly(ethylene glycol) with molecular weight of 300 and 1000 Da. The films were obtained by solution casting, cut in strips of (2x2) cm and buried in garden soil, monitoring the temperature and humidity. After 90, 120 and 150 days changes were observed in the films by visual inspection, polarized light microscopy, thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR). The results showed that the addition of surfactant favored the biodegradation of nanocomposites and that PLA/CNW/PEG1000 showed the fastest biodegradation rate.

ao meio ambiente, é uma alternativa mais promissora para minimizar a poluição derivada dos plásticos.Os poliésteres são polímeros biodegradáveis contendo grupos funcionais ésteres em sua estrutura. A principal razão é que as estruturas desses materiais são facilmente atacadas por fungos através de hidrólise [9] . Esses polímeros podem oferecer uma grande variedade de propriedades, desde plásticos rígidos altamente cristalinos a polímeros dúcteis. As propriedades terapêuticas descobertas em certos poliésteres possibilitaram sua produção em escala industrial, principalmente na forma de fios para suturas e cápsulas de comprimidos. Entre os polímeros biodegradáveis o mais conhecido é o poli(β-hidroxibutirato) (PHB) e seu copolímero poli(β-hidroxibutirato-co-valerato), ambos são produzidos por um processo de fermentação bacteriana, sendo ainda um processo relativamente caro [4,13] . Esses plásticos levam IntroduçãoO uso dos polímeros tem se tornado cada vez mais freqüente na sociedade moderna. Devido às suas propriedades e facilidade no processamento, torna-se um material adequado para ser usado nas mais diversas aplicações. Os polímeros são materiais inertes e não degradáveis, higiênicos, convenientes e confortáveis, no entanto, do ponto de vista ambiental, apresentam uma propriedade indesejável: a durabilidade. Pelo fato de algumas de suas aplicações serem de descartabilidade muito rápida, associado à grande dificuldade de degradação no meio ambiente, eles têm despertado forte preocupação nos dias atuais [2] . O desenvolvimento de novos materiais plásticos que sejam estáveis durante seu tempo de uso e biodegradável, especialmente por ação de microrganismo, quando descartado A Biodegradabilidade da Blenda de Poli(β-Hidroxibutirato-coValerato)/Amido Anfótero na Presença de Microrganismos Nadjane S. Coelho, Yêda M. B. Almeida, Glória M. Vinhas Departamento de Engenharia Química, UFPE Resumo: O crescimento do consumo de plásticos vem gerando grandes problemas ambientais, pois um polímero, uma vez descartado no ambiente, necessita de mais de cem anos para se degradar. O plástico ideal deve apresentar propriedades industriais desejáveis e, ao mesmo tempo ser degradável num período considerado satisfatório. Busca-se desenvolver plásticos com boas propriedades para embalagens e que possam ser biodegradados quando descartados ao ambiente. Neste trabalho avaliamos a biodegradação da blenda do copolímero poli(β-hidroxibutirato-co-valerato), PHB-HV, que é um termoplástico natural, biodegradável e biocompatível, e do amido anfótero, na proporção de 75 e 25% m/m, respectivamente. Os resultados foram obtidos através do teste de Sturm, uma metodologia para a avaliação da biodegradação na presença de uma cultura mista dos fungos Phanerochaete chrysosporium e Talaromyces wortmannii. Os resultados evidenciam a biodegradação da blenda em função do tempo, de acordo com os resultados do teste de Sturm, com o aparecimento de grupos carboxílicos terminais. Foi detectado também o aparecimento de nova simetria cristalina na estrutura polimé...