Silver nanoparticle-modified graphene oxide (Ag/GO) was reliably prepared by using sodium borohydride (NaBH4) in the presence of citric acid capping agent via a simple wet chemistry method. This rapidly formed Ag/GO composite exhibited good dispersity in a solution containing hydrophilic polyacrylonitrile (PAN). Subsequent electrospinning of this precursor solution resulted in the successful formation of nanofibers without any notable defects. The Ag/GO-incorporated PAN nanofibers showed thinner fiber strands (544 ± 82 nm) compared to those of GO-PAN (688 ± 177 nm) and bare-PAN (656 ± 59 nm). Subsequent thermal treatment of nanofibers resulted in the preparation of thin membranes to possess the desired pore property and outstanding wettability. The Ag/GO-PAN nanofiber membrane also showed 30% higher water flux value (390 LMH) than that of bare-PAN (300 LMH) for possible microfiltration (MF) application. In addition, the resulting Ag/GO-PAN nanofiber membrane exhibited antibacterial activity against Escherichia coli (Gram-negative) and Staphylococcus aureus (Gram-positive). Furthermore, this composite membrane exhibited outstanding anti-fouling property compared to the GO-PAN nanofiber membrane in the wastewater treatment. Therefore, the simple modification strategy allows for the effective formation of Ag/GO composite as a filler that can be reliably incorporated into polymer nanofiber membranes to possess improved overall properties for wastewater treatment applications.

CeOx hybrid nanoparticles were synthesized and evaluated for use as radical scavengers, in place of commercially available Ce(NO3)3 and CeO2 nanoparticles, to avoid deterioration of the initial electrochemical performance and/or spontaneous aggregation/precipitation issues encountered in polymer electrolyte membranes. When CeOx hybrid nanoparticles were used for membrane formation, the resulting membranes exhibited improved proton conductivity (improvement level = 2–15% at 30–90 °C), and thereby electrochemical single cell performance, because the –OH groups on the hybrid nanoparticles acted as proton conductors. In spite of a small amount (i.e., 1.7 mg/cm3) of introduction, their antioxidant effect was sufficient enough to alleviate the radical-induced decomposition of perfluorinated sulfonic acid ionomer under a Fenton test condition and to extend the chemical durability of the resulting reinforced membranes under fuel cell operating conditions.