Oxide (Nextel™ 440) fiber‐reinforced silica composites, with the density and porosity of 1.97 g/cm3 and 21.8%, were prepared through sol‐gel. Their average flexure strength, elastic modulus, shear strength, and fracture toughness at room temperature were 119.7 MPa, 25.6 GPa, 10.8 MPa, and 4.0 MPa·m1/2, respectively. The composites showed typical toughened fracture behavior, and distinct pullout fibers were observed at the fracture surface. Their mechanical properties were performant up to 1000°C, with the maximum flexural strength of 132.2 MPa at 900°C. Moreover, the composites showed good thermal stability, even after thermal aging and thermal shock at elevated temperatures.