No abstract

Lignocellulosic biomass is an abundant and renewable resource for the production of biobased value‐added fuels, chemicals, and materials, but its effective exploitation by an energy‐efficient and environmentally friendly strategy remains a challenge. Herein, a facile approach for efficiently cleaving lignin–carbohydrate complexes and ultrafast fractionation of components from wood by microwave‐assisted treatment with deep eutectic solvent is reported. The solvent was composed of sustainable choline chloride and oxalic acid dihydrate, and showed a hydrogen‐bond acidity of 1.31. Efficient fractionation of lignocellulose with the solvent was realized by heating at 80 °C under 800 W microwave irradiation for 3 min. The extracted lignin showed a low molecular weight of 913, a low polydispersity of 1.25, and consisted of lignin oligomers with high purity (ca. 96 %), and thus shows potential in downstream production of aromatic chemicals. The other dissolved matter mainly comprised glucose, xylose, and hydroxymethylfurfural. The undissolved material was cellulose with crystal I structure and a crystallinity of approximately 75 %, which can be used for fabricating nanocellulose. Therefore, this work promotes an ultrafast lignin‐first biorefinery approach while simultaneously keeping the undissolved cellulose available for further utilization. This work is expected to contribute to improving the economics of overall biorefining of lignocellulosic biomass.

Cellulose nanofibers (CNFs) were isolated from four kinds of plant cellulose fibers by a chemical-ultrasonic treatment. The chemical composition, morphology, crystalline behavior, and thermal properties of the nanofibers and their intermediate products were characterized and compared. The CNFs extracted from wood, bamboo, and wheat straw fibers had uniform diameters of 10-40 nm, whereas the flax fibers were not uniformly nanofibrillated because of their initially high cellulose content. The chemical composition of each kind of nanofibers was mainly cellulose because hemicelluloses and lignin were significantly removed during chemical process. The crystallinity of the nanofibers increased as the chemical treatments were applied. The degradation temperature of each kind of nanofiber reached beyond 330°C. Based on the properties of the CNFs, we expect that they will be suitable for use in green nanocomposites, filtration media and optically transparent films.

This article describes the fabrication of nanocellulose fibers (NCFs) with different morphologies and surface properties from biomass resources as well as their self-aggregation into lightweight aerogels. By carefully modulating the nanofibrillation process, four types of NCFs could be readily fabricated, including long aggregated nanofiber bundles, long individualized nanofibers with surface C6 -carboxylate groups, short aggregated nanofibers, and short individualized nanofibers with surface sulfate groups. Free-standing lightweight aerogels were obtained from the corresponding aqueous NCF suspensions through freeze-drying. The structure of the aerogels could be controlled by manipulating the type of NCFs and the concentration of their suspensions. A possible mechanism for the self-aggregation of NCFs into two- or three-dimensional aerogel nanostructures was further proposed. Owing to web-like structure, high porosity, and high surface reactivity, the NCF aerogels exhibited high mechanical flexibility and ductility, and excellent properties for water uptake, removal of dye pollutants, and the use as thermal insulation materials. The aerogels also displayed sound-adsorption capability at high frequencies.

With the aid of DFT calculation, deep eutectic solvents can be designed more powerful for the pretreatment of lignocellulose and the production of biochemicals.