The synthesis, characterization and catalytic capability of the NiW-nano-hydroxyapatite (NiW-nHA) composite were investigated in this paper. The NiW-nHA catalyst was prepared by a co-precipitation method. Then Fourier transform infrared (FT-IR) spectroscopy, transmission electron microscopy (TEM), X-ray diffraction (XRD) and energy dispersive spectroscopy (EDX) were used to analyze this material. In addition, the catalytic capacity of the NiW-nHA composite was also examined by FT-IR and gas chromatography (GC). The results of FT-IR analysis indicated that Ni, W and nHA combined closely. TEM observation revealed that this catalyst was needle shaped and the crystal retained a nanometer size. XRD data also suggested that a new phase of CaWO(4) appeared and the lattice parameters of nHA changed in this system. nHA was the carrier of metals. The rates of Ni/W-loading were 73.24% and 65.99% according to the EDX data, respectively. Furthermore, the conversion of 91.88% Jatropha oil was achieved at 360 °C and 3 MPa h(-1) over NiW-nHA catalyst. The straight chain alkanes ranging from C(15) to C(18) were the main components in the production. The yield of C(15)-C(18) alkanes was up to 83.56 wt%. The reaction pathway involved hydrocracking of the C═C bonds of these triglycerides from Jatropha oil. This paper developed a novel non-sulfided catalyst to obtain a "green biofuel" from vegetable oil.

Poly(lactide-co-glycolide) acid (PLGA) has been widely used as a biodegradable polymer material for coating stents or fabricating biodegradable stents. Its mechanism of degradation has been extensively investigated, especially with regard to how tensile and compressive loadings may affect the in vitro degradation of PLGA. Fluid shear stress is also one of the most important factors in the development of atherosclerosis and restenosis. But the effect of fluid shear stress on the degradation process is still unclear. The purpose of this study was to characterize the in vitro degradation of PLGA membranes that experienced different fluid shear stresses in 150 mL of deionized water at 37°C for 20 days. Particular emphasis was given to changes in the viscosity of the degradation solution, as well as the mechanical and morphological properties of the samples. The viscosity of the degradation solution with the mechanical loaded specimens was more severely affected than that of the control group. Increasing the fluid shear stress could accelerate the loss of the ultimate strength of PLGA membranes while it slowed down the change of the tensile elastic modulus in the early period. With regard to morphology, the surface roughness was more obviously reduced in the loaded groups. This indicated that the fluid shear stress could affect the in vitro degradation of PLGA membranes. Therefore, this study could help improve the design of PLGA membranes for biomedical applications. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A, 2016.

No abstract