The results of an experimental investigation on the physical and chemical characteristics of cement-based materials under laser interactions are presented. The laser cutting tests were conducted using a multi-mode continuous fiber laser with a laser power of 1 kW. The experimental variables were laser speed, water to cement ratio, and material compositions including cement paste, cement mortar, and ultra high-performance concrete (UHPC). In order to evaluate the mass removal mechanisms of cement-based materials under laser interactions, the effect of laser cutting was evaluated in terms of kerf width, penetration depth, and chemical composition changes before and after the interaction with laser using EDX analysis. The test results reveal that adding silica sand in cement-based materials leads to decreasing penetration depth and increasing kerf width. Unlike the cement paste and cement mortar series, UHPC specimens showed no discernible crack observed by the naked eye after laser interaction due to its high strength. Furthermore, the chemical analysis indicates that chemical composition changes were caused by various mechanisms including dehydration of calcium hydroxide and thermal decomposition of calcium carbonate.
We investigated the effect of simultaneous mechanical and electrical stress on the electrical characteristics of flexible indium-gallium-zinc oxide (IGZO) thin-film transistors (TFTs). The IGZO TFTs exhibited a threshold voltage shift (∆VTH) under an application of positive-bias-stress (PBS), with a turnaround behavior from the positive ∆VTH to the negative ∆VTH with an increase in the PBS application time, whether a mechanical stress is applied or not. However, the magnitudes of PBS-induced ∆VTH in both the positive and negative directions exhibited significantly larger values when a flexible IGZO TFT was under mechanical-bending stress than when it was at the flat state. The observed phenomena were possibly attributed to the mechanical stress-induced interface trap generation and the enhanced hydrogen diffusion from atomic layer deposition-grown Al2O3 to IGZO under mechanical-bending stress during PBS. The subgap density of states was extracted before and after an application of PBS under both mechanical stress conditions. The obtained results in this study provided potent evidence supporting the mechanism suggested to explain the PBS-induced larger ∆VTHs in both directions under mechanical-bending stress.
Cement-based materials are the most prevalent construction materials, and the conventional cutting techniques are still mostly used for fabricating the materials. However, these conventional cutting methods could generate undesirable micro-cracks and remove unintentional structural sections. This experimental study aims to evaluate the effects of the new fabricating method using laser on the microstructural characteristics of the cement-based materials. The experimental variables are laser cutting speed, water to cement ratio and material compositions. In order to compare the microstructure before and after the laser interaction, the microstructure of the cut surface is observed through scanning electron microscopy/energy dispersive X-Ray (SEM/EDX). After the laser interaction, the Material Removed Zone (MRZ) and Heat Affected Zone (HAZ) are observed on the cut surface. In MRZ, it is found that the glassy layer is thickened by an increasing amount of silicate-based materials in cement-based materials. In addition, it concluded that the amount of silicate-based material mixed in the cement-based materials affects the laser cutting quality.
This experimental research highlights the applicability of laser cutting to cement-based materials using multimode fiber lasers. A 9 kW multimode fiber laser is used, and the experimental variables are the water-to-cement ratio, laser speed, and material compositions such as cement paste, cement mortar and ultra high performance concrete (UHPC). The laser cutting performance on the cement-based materials is investigated in the downward laser direction. The kerf width and penetration depth of the cement-based materials are quantitatively evaluated with the parameters in the surface and cross section of the specimens after the laser cutting. Moreover, the material removal zone of each specimen is compared in terms of the penetration shapes in the cross-sectional view. Based on experimental observations, the interaction mechanism between the laser and cement-based materials is proposed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.