coatings were prepared by deposition of Cu layer between two Ni-P layers. The Cu layer was deposited by metal displacement reaction between Cu 2+ and Fe atoms. Corrosion behavior of single-layer Ni-P coatings, double-layer Ni-P/Cu coatings, and three-layer Ni-P/Cu/Ni-P coatings were investigated by electrochemical tests in 3.5% NaCl solution. The three-layer coatings exhibited more positive E corr and decreased I corr compared with conventional single-layer Ni-P coatings, which indicated an improved corrosion resistance. The polarization curves of the three-layer coatings were characterized by two passive regions. The improved corrosion resistance was not only attributed to the function of the blocked pores of Cu. The Cu interlayer also acted as a sacrificial layer instead of a barrier in the coatings, which altered the corrosion mechanism and further improved the corrosion resistance of the coatings.Keywords: electroless plating, multilayer coatings, porosity, electrochemical tests, crystalline Cu layerWielowarstwowe powłoki Ni-P/Cu/Ni-P wytworzono metodą osadzania miedzi pomiędzy dwoma warstwami Ni-P. Warstwę Cu otrzymano dzięki reakcji wypierania metalu przez metal (dla miedzi i żelaza). Aby określić właściwości korozyjne jednowarstwowej powłoki Ni-P, dwuwarstwowej Ni-P/Cu oraz trójwarstwowej Ni-P/Cu/Ni-P przeprowadzono pomiary elektrochemiczne w 3,5% roztworze NaCl. Powłoki trójwarstwowe w porównaniu do jednowarstwowych wykazały się większą wartością E corr , przy malejącej wartości I corr . Wskazuje to na poprawę odporności na korozję. Krzywe polaryzacji dla powłok trójwarstwowych charakteryzują się występowaniem dwóch obszarów pasywacji. Poprawa odporności na korozję jest skutkiem nie tylko tzw. zjawiska blokowania porów w miedzi. Powłoka z Cu działała także jako warstwa protektorowa, modyfikując mechanizm korozji i poprawiając odporność korozyjną powłok.