A synthetic mimic of mussel adhesive protein, dopamine-modified four-armed poly(ethylene glycol) (PEG-D4), was combined with a synthetic nanosilicate, Laponite (Na0.7+(Mg5.5Li0.3Si8)O20(OH)4)0.7–), to form an injectable naoncomposite tissue adhesive hydrogel. Incorporation of up to 2 wt % Laponite significantly reduced the cure time while enhancing the bulk mechanical and adhesive properties of the adhesive due to strong interfacial binding between dopamine and Laponite. The addition of Laponite did not alter the degradation rate and cytocompatibility of PEG-D4 adhesive. On the basis of subcutaneous implantation in rat, PEG-D4 nanocomposite hydrogels elicited minimal inflammatory response and exhibited an enhanced level of cellular infiltration as compared to Laponite-free samples. The addition of Laponite is potentially a simple and effective method for promoting bioactivity in a bioinert, synthetic PEG-based adhesive while simultaneously enhancing its mechanical and adhesive properties.

Due to the increasing needs for organ transplantation and a universal shortage of donated tissues, tissue engineering emerges as a useful approach to engineer functional tissues. Although different synthetic materials have been used to fabricate tissue engineering scaffolds, they have many limitations such as the biocompatibility concerns, the inability to support cell attachment, and undesirable degradation rate. Fibrin gel, a biopolymeric material, provides numerous advantages over synthetic materials in functioning as a tissue engineering scaffold and a cell carrier. Fibrin gel exhibits excellent biocompatibility, promotes cell attachment, and can degrade in a controllable manner. Additionally, fibrin gel mimics the natural blood-clotting process and self-assembles into a polymer network. The ability for fibrin to cure in situ has been exploited to develop injectable scaffolds for the repair of damaged cardiac and cartilage tissues. Additionally, fibrin gel has been utilized as a cell carrier to protect cells from the forces during the application and cell delivery processes while enhancing the cell viability and tissue regeneration. Here, we review the recent advancement in developing fibrin-based biomaterials for the development of injectable tissue engineering scaffold and cell carriers.

The remarkable underwater adhesion strategy employed by mussels has inspired bioadhesives that have demonstrated promise in connective tissue repair, wound closure, and local delivery of therapeutic cells and drugs. While the pH of oxygenated blood and internal tissues is typically around 7.4, skin and tumor tissues are significantly more acidic. Additionally, blood loss during surgery and ischemia can lead to dysoxia, which lowers pH levels of internal tissues and organs. Using 4-armed PEG end-capped with dopamine (PEG-D) as a model adhesive polymer, the effect of pH on the rate of intermolecular cross-linking and adhesion to biological substrates of catechol-containing adhesives was determined. Adhesive formulated at an acidic pH (pH 5.7–6.7) demonstrated reduced curing rate, mechanical properties, and adhesive performance to pericardium tissues. Although a faster curing rate was observed at pH 8, these adhesives also demonstrated reduced mechanical and bioadhesive properties when compared to adhesives buffered at pH 7.4. Adhesives formulated at pH 7.4 demonstrated a good balance of fast curing rate, elevated mechanical properties and interfacial binding ability. UV–vis spectroscopy evaluation revealed that the stability of the transient oxidation intermediate of dopamine was increased under acidic conditions, which likely reduced the rate of intermolecular cross-linking and bulk cohesive properties for hydrogels formulated at these pH levels. At pH 8, competing cross-linking reaction mechanisms and reduced concentration of dopamine catechol due to auto-oxidation likely reduced the degree of dopamine polymerization and adhesive strength for these hydrogels. pH plays an important role in the adhesive performance of mussel-inspired bioadhesives and the pH of the adhesive formulation needs to be adjusted for the intended application.

Engineering bioadhesives to bind and conform to the complex contour of tissue surfaces remains a challenge. We developed a novel moldable nanocomposite hydrogel by combining dopamine-modified poly(ethylene glycol) and nano-silicate, Laponite, without using cytotoxic oxidants. The hydrogel transitioned from a reversibly crosslinked network formed from dopamine-Laponite interfacial interactions to a covalently crosslinked network through the slow autoxidation and crosslinking of catechol moieties. Initially, the hydrogel can be remolded to different shapes, can recover from large strain deformation, and can be injected through a syringe to adhere to the convex contour of a tissue surface. With time, the hydrogel solidified to adopt the new shape and sealed defects on the tissue. This fit-to-shape sealant has potential in sealing tissues with non-flat geometries, such as a sutured anastomosis.

Dopamine mimics the exceptional moisture-resistant adhesive properties of the amino acid, DOPA, found in adhesive proteins secreted by marine mussels. The catechol side chain of dopamine was functionalized with a nitro-group, and the effect of the electron withdrawing group modification on the cross-linking chemistry and bioadhesive properties of the adhesive moiety was evaluated. Both nitrodopamine and dopamine were covalently attached as a terminal group onto an inert, 4-armed poly(ethylene glygol) (PEG-ND and PEG-D, respectively). PEG-ND and PEG-D exhibited different dependence on the concentration of NaIO4 and pH, which affected the curing rate, mechanical properties, and adhesive performance of these biomimetic adhesives differently. PEG-ND cured instantly and its bioadhesive properties were minimally affected by the change in pH (5.7–8) within the physiological range. Under mildly acidic conditions (pH 5.7 and 6.7), PEG-ND outperformed PEG-D in lap shear adhesion testing using wetted pericardium tissues. However, nitrodopamine only formed dimers, which resulted in the formation of loosely cross-linked network and adhesive with reduced cohesive properties. UV–vis spectroscopy further confirmed nitrodopamine’s ability for rapid dimer formation. The ability for nitrodopamine to rapidly cure and adhere to biological substrates in an acidic pH make it suitable for designing adhesive biomaterials targeted at tissues that are more acidic (i.e., subcutaneous, dysoxic, or tumor tissues).