Microstructure evolution of Ag28Cu1Ni alloy during the continuous casting process was simulated based on 3D-CAFE method, and the effect of the mean nucleation undercooling and the distance from the bottom of the ingot to the cross section on the solidification structure were studied. Furthermore, the effects of pouring temperature, heat transfer coefficient and pulling speed on solidification structure were also investigated. The results show that the simulated results are in agreement with the experimental results. The solidification structure consists of four parts, including region of surface fine grain, zone of columnar grain, transition zone of CET (columnar to equiaxed grain transition) and region of center equiaxed grain. The higher the mean undercooling, the larger the columnar dendrite zone. The ¦T v,max = 5 K is determined as an important simulation parameter to simulate the microstructure evolution. As the cross-section increases from the bottom of the ingot, the columnar crystal regions gradually expand. Moreover, lowering the pouring temperature, increasing the heat transfer coefficient or improving the pulling speed have the beneficial effect on grain refinement. Under the optimal process conditions, the largest proportion of equiaxed grains and the finer grain size is present in the solidified structure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.