In this study, the wear failure behaviour of coated self-lubricating spherical plain bearings under different working conditions in the light-load and low-frequency range was studied using a swing wear life tester. The commercial GE17ES bearing was the main research object, and the wear state of the bearing was monitored in real time using torque and temperature rise signals. Furthermore, a scanning electron microscope and an energy dispersive X-ray spectroscope were adopted to analyse the wear failure mechanism of bearings. The results indicated that the friction torque and temperature rise signal changes were mainly divided into three stages, and the characteristics of similar changes could be maintained under different working conditions. Furthermore, at the end of the bearing life, the torque and temperature rise had abrupt changes almost at the same time, which indicated the occurrence of bearing failure. In general, the wear failure mechanisms of bearings included abrasive wear and adhesive wear. Moreover, fatigue wear and oxidation wear were under some conditions. The torque and temperature rise comprehensively reflected the service state of coated self-lubricating spherical plain bearings, which could be used as a physical criterion for determining bearing failure. These results had a strong prospect of engineering application, and were expected to provide a reference for determining the failure behaviour of multi-type coated self-lubricating spherical plain bearings in the future, and provided theoretical support for establishing relevant test standards.

No abstract

No abstract

No abstract

In order to explore the influence of space ultraviolet radiation on spacecraft lubricating materials, an in-situ friction experimental device simulating space ultraviolet radiation was developed in the laboratory, and the experimental verification was carried out. This paper firstly introduced the design index, structure and working principle of the space ultraviolet irradiation simulation device, and then calibrated and tested the parameters of the whole device, and also conducted a virtual operation of the device’s operation effect by simulation software, and the results showed that it met the design index. Finally, the validation tested of the ultraviolet irradiated in-situ friction experimental device were described in detail. By using the device to irradiate the samples, it was found that the in-situ ultraviolet irradiation device could achieve the expected irradiation effect, and the irradiation would lead to changes in the surface structure and properties of the PTFE material, while also achieving the need for in-situ spatial friction property testing of the material, providing favorable conditions for future testing.