For the inverted organic solar cells (OSCs), the interface contacts between the ZnO electron transporting layer and the organic active layer play an important role in the device performance and stability. Since the solution-processed ZnO surface always contains some base or zinc salt contaminants, we explored how the surface pH conditions influence the performance and stability of the nonfullerene acceptor (NFA) cells. A tight relationship between the surface pH condition and the device performance and stability was established. Specifically, device performance and stability were improved by treating the ZnO films with acid solutions but worsened after base treatment. The large number of hydroxyl groups on the surface of the solution-processed ZnO films was proved to be the main reason for the surface pH condition-related performance, which caused oxygen-deficient defects and unfavorable vertical phase separation in the blend films, hindered the photogenerated charge transfer and collection, and consequently resulted in low short-circuit current density and power conversion efficiency (PCE). The surface −OH groups also boosted the photocatalytic activity and led to fast degradation of the nonfullerene acceptor. Removal of the surface −OH groups can alleviate such problems. Different acid solutions, ZrAcac, 2-phenylethylmercaptan (PET), and glutamic acid (GC), were used to treat the ZnO films, and PET treatment was the most effective treatment for performance improvement. An efficiency of 16.46% was achieved for the PM6:Y6 cells and the long-term stability under continuous illumination conditions was significantly improved with a T 80 lifetime of over 4000 h (4410 h), showing the excellent long-term stability of this heterojunction solar cell. Our understanding of the surface pH condition-related device performance and stability would guide the development of a feasible method for solving the interface problems in OSCs. We also provide a practical strategy to modify ZnO with acid solutions for high-performance and stable NFA OSCs.
With the aim of developing high‐performance flexible polymer solar cells, the preparation of flexible transparent electrodes (FTEs) via a high‐throughput gravure printing process is reported. By varying the blend ratio of the mixture solvent and the concentration of the silver nanowire (AgNW) inks, the surface tension, volatilization rate, and viscosity of the AgNW ink can be tuned to meet the requirements of gravure printing process. Following this method, uniformly printed AgNW films are prepared. Highly conductive FTEs with a sheet resistance of 10.8 Ω sq−1 and a high transparency of 95.4% (excluded substrate) are achieved, which are comparable to those of indium tin oxide electrode. In comparison with the spin‐coating process, the gravure printing process exhibits advantages of the ease of large‐area fabrication and improved uniformity, which are attributed to better ink droplet distribution over the substrate. 0.04 cm2 polymer solar cells based on gravure‐printed AgNW electrodes with PM6:Y6 as the photoactive layer show the highest power conversion efficiency (PCE) of 15.28% with an average PCE of 14.75 ± 0.35%. Owing to the good uniformity of the gravure‐printed AgNW electrode, the highest PCE of 13.61% is achieved for 1 cm2 polymer solar cells based on the gravure‐printed FTEs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.