A series of graphene-based nanocomposites with different TiO2 contents have been prepared via a facile chemical method.

High-specific-surface-area MgF2 was prepared by microwave-assisted solvothermal synthesis. The influences of the solvent and the magnesium precursors, and the calcination atmospheres, on the nanoparticle sizes and specific surface areas, estimated by X-Ray Powder Diffraction, N2 sorption and TEM analyses, were investigated. Nanocrystallized (~7 nm) magnesium partially hydroxylated fluorides (MgF2−x(OH)x) with significant specific surface areas between 290 and 330 m2∙g−1 were obtained. After activation under gaseous HF, MgF2−x(OH)x catalysts underwent a large decrease of both their surface area and their hydroxide, rates as shown by their 19F and 1H solid-state NMR spectra. Expect for MgF2 prepared from the acetate precursor, an activity of 30–32 mmol/h∙g was obtained which was about 40% higher compared with that of MgF2 prepared using Trifluoroacetate method (21.6 mmol/h∙g).

No abstract

In this study, graphene nanoplatelets (GNPs) were incorporated into poly(vinylidene fluoride) (PVDF), poly(ethylene oxide) (PEO), and PVDF/PEO blends using solution casting method in order to achieve binary and ternary polymer nanocomposites. The focus of the work is on the compatibilizing effects of the GNPs on partially miscible PVDF/PEO blends. X‐ray diffraction method, rheological measurements, scanning electron microscopy (SEM), and atomic force microscopy observations enabled us to track the dispersion state and localization of the graphene nanosheets in the nanocomposites. The results exhibited that the nanoplatelets were preferentially distributed through the PVDF phase and/or at the interface of the PVDF/PEO phases. Evaluation of the wetting parameter for the PVDF/PEO/GNPs nanocomposite also verified better affinity of the selected nanofiller with the PVDF component. Extend of the miscibility in the nanocomposites was studied by a well‐known rheological method. A tangible increment in binodal (Tb) and spinodal (Ts) decomposition temperatures by addition of a very low content of the GNPs (0.5 wt %) revealed well‐defined compatibilization effects of the graphene on this binary polymer blend. SEM images at different temperatures confirmed the rheologically determined liquid–liquid phase diagram. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 48017.