Increasing environmental awareness and concern have shifted the focus of research and development towards biodegradable materials development. In the current study, Cymbopogan citratus fibre (CCF) were incorporated into thermoplastic cassava starch (TPCS) with various content of CCF (10, 20, 30, 40, 50, 60 wt.%) via compression moulding. The determination of fundamental characteristics of TPCS/CCF biopolymer composites was conducted to assess their potential as biodegradable reinforcements. Characterization of the samples was conducted via Fourier-transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM), as well as mechanical, moisture absorption, and soil burial testings. The findings showed that the improved tensile and flexural features of the TPCS composites with CCF incorporation, with 50 wt.% CCF content yielded the maximum modulus and strength. The thermal properties of the biocomposite demonstrated that CCF addition improved the material’s thermal stability, as shown by a higher-onset decomposition temperature and ash content. Meanwhile, the CCF incorporation into TPCS slowed down the biodegradation of the composites. In term of morphological, homogeneous fibres and matrix dispersion with excellent adhesion was observed in morphological analyses using scanning electron microscopy (SEM), which is crucial for the enhancement of the mechanical performance of biocomposites.
A novel natural fiber derived from the Cymbopogan citratus plant was investigated for the first time. The characterization of the C. citratus fibers was conducted, and the chemical composition and physical, thermal, mechanical, crystallinity, and morphological characteristics were studied. The chemical composition analysis of Cymbopogan citratus fiber revealed that the suggested fiber was rich in cellulose contents (37.6%). The tensile test of C. citratus fiber demonstrated the fiber’s average tensile strength of 43.81 ± 15.27 MPa and modulus of elasticity of 1.046 ± 0.33 GPa. Further analysis with X-ray diffraction (XRD) confirmed that the crystallinity index of Cymbopogan citratus fiber was 35.2%, and the crystalline size was estimated as 4.28 nm. The Cymbopogan citratus fiber’s thermal stability was investigated via thermogravimetric analysis (TGA) and observed to be thermally stable (230 °C). A morphological investigation was employed on the fiber via a scanning electron microscope (SEM). The morphological study result exhibited that the fiber had a perforated and rough surface with the lumen in the center. Thus, the findings revealed that the Cymbopogan citratus fiber was a promising potential reinforcement for thermoplastic green composite applications.
In this study, thermoplastic cassava starch–palm wax blends, reinforced with the treated Cymbopogan citratus fiber (TPCS/ PW/ CCF) were successfully developed. The TPCS were priorly modified with palm wax to enhance the properties of the matrix. The aim of this study was to investigate the influence of alkali treatments on the TPCS/PW/CCF biocomposite. The fiber was treated with different sodium hydroxide (NaOH) concentrations (3%, 6%, and 9%) prior to the composite preparation via hot pressing. The obtained results revealed improved mechanical characteristics in the treated composites. The composites that underwent consecutive alkali treatments at 6% NaOH prior to the composite preparation had higher mechanical strengths, compared to the untreated fibers. A differential scanning calorimetry (DSC) and a thermogravimetric analysis (TGA) indicated that adding treated fibers into the TPCS matrix improved the thermal stability of the samples. The scanning electron microscopy (SEM) demonstrated an improved fiber–matrix adhesion due to the surface modification. An increment in the glass transition temperature (Tg) of the composites after undergoing NaOH treatment denoted an improved interfacial interaction in the treated samples. The Fourier transform infrared spectroscopy (FTIR) showed the elimination of hemicellulose at wavelength 1717 cm−1, for the composites treated with 6% NaOH. The water absorption, solubility, and thickness swelling revealed a higher water resistance of the composites following the alkali treatment of the fiber. These findings validated that the alkaline treatment of CCF is able to improve the functionality of the Cymbopogan citratus fiber-reinforced composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.