The effects of the composition alteration on the magnetization and shape memory behavior of Ni50Mn40-xSn10+x (x=0, 1, 2, 3) alloys were systematically investigated by thermal, magnetic and mechanical experiments. Phase transformation from ferromagnetic austenite to weakly magnetic martensite was observed during thermal cycling under magnetic field and transformation temperatures were decreased with increasing Sn (or decreasing Mn). Moreover, the saturation magnetization of martensite increased with Sn content. Ni50Mn40Sn10 showed the recoverable strain of 2.1 % during thermal cycling under 300 MPa and the reversible superelastic strain of 2 % at 190 °C. Mechanical experiments exhibited that the largest compressive deformation of about 7 % at 650 MPa occurred in Ni50Mn39Sn11 while Ni50Mn40Sn10 had fractured at 4 % and 390 MPa at room temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.