This work provides a facile method to regulate swelling properties and/or to impart special functions for click poly(N-isopropylacrylamide) (PNIPA) hydrogels, by adjusting the chain length of crosslinkers or by introducing other functional groups.

We designed and synthesized a novel high efficiency Cr(VI) removal material using reduced graphene oxide (RGO) as a support with high specific surface area and a mixture of Fe and Ni nanoparticles (NPs) as a catalytic reducing agent. Such a design enables the composite particle to be integrated with three functions of adsorption, catalysis, and reduction, where RGO could enhance Cr(VI) adsorption, while Fe/Ni NPs increase the catalytic reducing efficiency. The application of a microchip mixer guaranteed a better mixing of GO and subsequent decoration of Fe and Ni NPs on RGO. Cr(VI) removal experiments with various materials are performed, and the results demonstrated that the Ni−Fe/RGO achieved an adsorption capacity of 150.45 mg/g at pH = 7 and 197.43 mg/g at pH = 5 for Cr(VI), which is higher than those of other reported materials at a pH of ∼7. To the best of our knowledge, this is the first example of Ni−Fe/RGO for efficient Cr(VI) removal by using the synergistic effects of increased adsorption, catalysis-assisted reduction, and enhanced mixing effect of a microchip mixer. This work also provides us with a simple and low-cost method for the fabrication of an effective Cr(VI) removal material.

A novel Cr (VI) removal material was designed and produced comprising multi-walled carbon nanotubes (MWCNTs) as a support with a high specific surface area and the loaded Fe–Ni bimetallic particles as catalytic reducing agents. Such a design permits the composite particle to perform the adsorption, reduction, and immobilisation of Cr (VI) quickly and efficiently. Due to MWCNTs’ physical adsorption, Cr (VI) in solution aggregates in the vicinity of the composite, and Fe rapidly reduces Cr (VI) to Cr (III) catalysed by Ni. The results demonstrated that the Fe–Ni/MWCNTs exhibits an adsorption capacity of 207 mg/g at pH = 6.4 for Cr (VI) and 256 mg/g at pH 4.8, which is about twice those reported for other materials under similar conditions. The formed Cr (III) is solidified to the surface by MWCNTs and remains stable for several months without secondary contamination. The reusability of the composites was proven by retaining at least 90% of the adsorption capacity for five instances of reutilization. Considering the facile synthesis process, low cost of raw material, and reusability of the formed Fe–Ni/MWCNTs, this work shows great potential for industrialisation.