Gold nanoparticles (3-4 nm) were deposited on Mn3O4 nanocrystallites with three distinct morphologies (cubic, hexagonal, and octahedral). The resulting structures were characterized, and their activities for benzene combustion were evaluated. The dominant exposed facets for the three kinds of Mn3O4 polyhedrons show the activity order: (103)≈(200)>(101). A similar activity order was derived for the interfaces between the Au and the Mn3O4 facet: Au/(200)≈Au/(103)>Au/(101). The metal-support interactions between the Au nanoclusters and specific facets of the Mn3O4 polyhedrons lead to a unique interfacial synergism in which the electronic modification of the Au nanoparticles and the morphology of the Mn3O4 substrate have a joint effect that is responsible for a significant enhancement in the catalytic activity of the Au/Mn3O4 system.

Lanthanum molybdate powders were prepared by sol-gel using lanthanum nitrate, ammonium molybdate, citric acid as the main raw materials. The prepared powders were characterized by XRD, SEM, BET and other methods. It is concluded that the best sintering temperature was 550°C, the aging time was 1h and the best ph value was 1.5.