The development behaviors of ultrafine grains (UFGs) due to continuous dynamic recrystallization (cDRX) were investigated in hot compression of a Mg-4Y-2Nd-0.2Zn-0.5Zr alloy pretreated in solution and subsequently peak-aging. In the aging sample containing statically precipitated particles (SPPs), the occurrence of cDRX starts to take place at medium to high strains, and finally a stable size of UFGs are fully developed in a whole volume. In the as-solution sample with no SPPs, by contrast, the size of UFGs evolved increases rapidly at lower strains, slowly at medium strains and then finally shows a bimodal distribution in high strain. In the latter, smaller grains accompanying with an incomplete formation of UFGs are developed by any effect of dynamically precipitated particles (DPPs). The microtexture evolved is effectively randomized in the regions of UFGs, leading to the formation of a weaker texture. The tensile elongation of the aging sample, with SPPs and a fully developed UFGs, was around 17.4 %. This was much higher than that of the as-solution one, with no SPPs and an incompletely developed UFGs, that was 11.8 %, which might result from the more randomized texture due to fully developed UFGs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.